Lanxess Durethan® AKV 35 H3.0 000000 Nylon 66, 35% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® AKV 35 H3.0 000000 Nylon 66, 35% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, injection molding grade, 35% glass fibers, good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Water Absorption | 5.0 % | 5.0 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 135 MPa | 19600 psi | Conditioned; ISO 527-1/-2 |
| 200 MPa | 29000 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| 5.0 % | 5.0 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 7.90 GPa | 1150 ksi | Conditioned; ISO 527-1/-2 |
| 11.8 GPa | 1710 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 9.50 J/cm² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 1027 | 1027 | Puncture maximum force (N); ISO 6603-2 |
| 906 @Temperature -30.0 °C |
906 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 3.90 J | 2.88 ft-lb | ISO 6603-2 |
| 2.80 J @Temperature -30.0 °C |
2.07 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 2.80 J @Temperature -30.0 °C |
2.07 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 | |
| Tensile Creep Modulus, 1 hour | 7000 MPa | 1.02e+6 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 5800 MPa | 841000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 263 °C | 505 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 155 °C | 311 °F | ISO 75-1/-2 |
| Vicat Softening Point | 230 °C | 446 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 23 % | 23 % | ISO 4589-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 66,MHR,14-120,GF35 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CX3222ME PC+ABS
- 3M Dyneon™ THV 510ESD Fluorothermoplastic (discontinued **)
- Kolon ELLAS K-787A Ester Based Thermoplastic Polyurethane
- Gouda Vuurvast AK 70 K Dense Refractory Brick
- Ferro F 1040 Metal Sealing
- Sichuan Deyang Haton® hGR40DL Polyphenylene Sulfide, Glass Fiber Reinforced
- Teknor Apex Beetle® 60GS6 Nylon 6, 30% Glass Bead Reinforced, Dry
- BCC Products BC 7062-2H Epoxy Casting
- Beijing Ranger Chem PBT 403 M-G50 Heat Resistant and Environmental Protection Flame Retarding FR PBT
- Plenco 50335 PET, Pellet, Injection Molded, Black (discontinued **)
Copyright © lookpolymers.com All Rights Reserved