DuPont Performance Polymers Rynite® FR530L NC010 Polyethylene Terephthalate (PET)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Rynite® FR530L NC010 Polyethylene Terephthalate (PET).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Rynite FR530 NC010 is a 30% glass reinforced flame retardant modified polyethylene terephthalate resin.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 |
| Water Absorption | 0.75 % @Thickness 2.00 mm |
0.75 % @Thickness 0.0787 in |
Sim. to ISO 62 |
| Moisture Absorption | 0.150 % @Thickness 2.00 mm |
0.150 % @Thickness 0.0787 in |
Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4 2577 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4 2577 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 280 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 536 °F |
cm³/10min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 135 MPa | 19600 psi | ISO 527-1/-2 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1/-2 |
| Tensile Modulus | 11.5 GPa | 1670 ksi | ISO 527-1/-2 |
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178 |
| Shear Modulus | 0.525 GPa @Temperature 160 °C |
76.1 ksi @Temperature 320 °F |
Dynamic; ISO 11403-1 -2 |
| 0.654 GPa @Temperature 120 °C |
94.9 ksi @Temperature 248 °F |
Dynamic; ISO 11403-1 -2 | |
| 1.151 GPa @Temperature 70.0 °C |
166.9 ksi @Temperature 158 °F |
Dynamic; ISO 11403-1 -2 | |
| 1.974 GPa @Temperature 20.0 °C |
286.3 ksi @Temperature 68.0 °F |
Dynamic; ISO 11403-1 -2 | |
| 2.208 GPa @Temperature -20.0 °C |
320.2 ksi @Temperature -4.00 °F |
Dynamic; ISO 11403-1 -2 | |
| 2.432 GPa @Temperature -50.0 °C |
352.7 ksi @Temperature -58.0 °F |
Dynamic; ISO 11403-1 -2 | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU |
| 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1 hour | 11200 MPa @Time 3600 sec |
1.62e+6 psi @Time 1.00 hour |
ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 9700 MPa @Time 3.60e+6 sec |
1.41e+6 psi @Time 1000 hour |
ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C | 10.6 µin/in-°F | ISO 11359-1/-2 |
| 22.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
12.2 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 92.0 µm/m-°C | 51.1 µin/in-°F | ISO 11359-1/-2 |
| 68.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |
| Melting Point | 252 °C | 486 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75-1/-2 |
| Vicat Softening Point | 220 °C | 428 °F | 50°C/h 50N; ISO 306 |
| UL RTI, Electrical | 155 °C @Thickness 0.400 mm |
311 °F @Thickness 0.0157 in |
UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
IEC 60695-11-10 |
| V-0 @Thickness 0.300 mm |
V-0 @Thickness 0.0118 in |
IEC 60695-11-10 | |
| 5VA @Thickness 0.900 mm |
5VA @Thickness 0.0354 in |
IEC 60695-11-20 | |
| Oxygen Index | 33 % | 33 % | ISO 4589-1/-2 |
| 33 % | 33 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.8 @Frequency 1000 Hz |
3.8 @Frequency 1000 Hz |
ASTM D150 | |
| 4.7 @Frequency 1.00e+6 Hz |
4.7 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 4.8 @Frequency 100 Hz |
4.8 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0070 @Frequency 100 Hz |
0.0070 @Frequency 100 Hz |
IEC 60250 |
| 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.011 @Frequency 1000 Hz |
0.011 @Frequency 1000 Hz |
ASTM D150 | |
| 0.018 @Frequency 1.00e+6 Hz |
0.018 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 |
| 250 - 400 V | 250 - 400 V | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Delivery Form | Pellets | |
| Part Marking Code | >PET-GF30FR< | ISO 11469 |
| Processing | Injection Moulding | |
| Regional Availability | Europe | |
| Near East/Africa | ||
| Resin Identification | PET-GF30FR(17) | |
| UL recognition | UL |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers AvaSpire® AV-848 GF30 Polyaryletherketone (PAEK) (Unverified Data**)
- IRPC Polimaxx Porene AN510 Acrylonitrile Butadiene Styrene
- Teknor Apex APEX® 90-A472R-65-NT Polyvinyl Chloride, Flexible
- Sumitomo Bakelite North America RX® 448 Cellulose Reinforced Phenolic Novolac
- Unifrax Fiberfrax® Vari-Form™ A Casting Mix
- Polyram PlusTek PA360G6 Nylon 6.6, 30% Glass Fiber
- Eurostar Starflam BFR460A PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
- China Tungsten YG15 Tungsten Carbide for Dies and Wear Part Making
- ExxonMobil Escorene® UL-7560 EVA Copolymer, Adhesive and Sealant Grade (discontinued **)
- Polyram RamOfin PPC371B50 Polypropylene, 50% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved