DuPont Performance Polymers Zytel® 73G15L NC010 Nylon 6  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 73G15L NC010 Nylon 6  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
15% Glass Reinforced Polyamide 6Zytel 73G15L NC010 is a 15% glass fiber reinforced polyamide 6 resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
1.23 g/cc
0.0444 lb/in³
DAM; ISO 1183
Water Absorption 7.6 %

@Thickness 2.00 mm
 7.6 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 2.50 %

@Thickness 2.00 mm
 2.50 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity Test 150 cm³/g
150 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 72.0 MPa
10400 psi
50%RH; ISO 527-1/-2
135 MPa
19600 psi
DAM; ISO 527-1/-2
Tensile Stress 4.30 MPa

@Strain 0.240 %,
Temperature 150 °C
 624 psi

@Strain 0.240 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
7.19 MPa

@Strain 0.270 %,
Temperature 40.0 °C
 1040 psi

@Strain 0.270 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
7.60 MPa

@Strain 0.250 %,
Temperature 23.0 °C
 1100 psi

@Strain 0.250 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
12.69 MPa

@Strain 0.620 %,
Temperature 150 °C
 1841 psi

@Strain 0.620 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
15.61 MPa

@Strain 1.08 %,
Temperature 150 °C
 2264 psi

@Strain 1.08 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
16.85 MPa

@Strain 0.330 %,
Temperature 0.000 °C
 2444 psi

@Strain 0.330 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
23.05 MPa

@Strain 2.05 %,
Temperature 150 °C
 3343 psi

@Strain 2.05 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
28.13 MPa

@Strain 3.05 %,
Temperature 150 °C
 4080 psi

@Strain 3.05 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
28.97 MPa

@Strain 0.400 %,
Temperature -40.0 °C
 4201 psi

@Strain 0.400 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
29.16 MPa

@Strain 1.85 %,
Temperature 150 °C
 4229 psi

@Strain 1.85 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
33.36 MPa

@Strain 1.49 %,
Temperature 40.0 °C
 4838 psi

@Strain 1.49 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
37.35 MPa

@Strain 1.43 %,
Temperature 23.0 °C
 5417 psi

@Strain 1.43 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
39.21 MPa

@Strain 3.13 %,
Temperature 150 °C
 5687 psi

@Strain 3.13 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
42.59 MPa

@Strain 0.810 %,
Temperature 40.0 °C
 6177 psi

@Strain 0.810 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
45.14 MPa

@Strain 4.46 %,
Temperature 150 °C
 6547 psi

@Strain 4.46 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
49.68 MPa

@Strain 2.64 %,
Temperature 40.0 °C
 7205 psi

@Strain 2.64 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
56.39 MPa

@Strain 2.57 %,
Temperature 23.0 °C
 8179 psi

@Strain 2.57 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
56.95 MPa

@Strain 0.900 %,
Temperature -20.0 °C
 8260 psi

@Strain 0.900 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
58.81 MPa

@Strain 1.32 %,
Temperature 0.000 °C
 8530 psi

@Strain 1.32 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
59.7 MPa

@Strain 3.93 %,
Temperature 40.0 °C
 8660 psi

@Strain 3.93 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
63.4 MPa

@Strain 1.10 %,
Temperature 23.0 °C
 9200 psi

@Strain 1.10 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
68.83 MPa

@Strain 3.84 %,
Temperature 23.0 °C
 9983 psi

@Strain 3.84 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
70.36 MPa

@Strain 1.44 %,
Temperature 40.0 °C
 10200 psi

@Strain 1.44 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
84.36 MPa

@Strain 1.46 %,
Temperature 0.000 °C
 12240 psi

@Strain 1.46 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
85.29 MPa

@Strain 2.35 %,
Temperature 0.000 °C
 12370 psi

@Strain 2.35 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
90.95 MPa

@Strain 2.07 %,
Temperature 40.0 °C
 13190 psi

@Strain 2.07 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
93.32 MPa

@Strain 1.60 %,
Temperature -20.0 °C
 13530 psi

@Strain 1.60 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
94.32 MPa

@Strain 1.74 %,
Temperature 23.0 °C
 13680 psi

@Strain 1.74 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
98.54 MPa

@Strain 1.69 %,
Temperature -20.0 °C
 14290 psi

@Strain 1.69 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
101.18 MPa

@Strain 3.43 %,
Temperature 0.000 °C
 14675 psi

@Strain 3.43 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
105.22 MPa

@Strain 2.84 %,
Temperature 40.0 °C
 15261 psi

@Strain 2.84 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
106.2 MPa

@Strain 1.60 %,
Temperature -40.0 °C
 15400 psi

@Strain 1.60 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
107.08 MPa

@Strain 1.94 %,
Temperature 0.000 °C
 15531 psi

@Strain 1.94 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
114.51 MPa

@Strain 2.25 %,
Temperature 23.0 °C
 16608 psi

@Strain 2.25 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
119.26 MPa

@Strain 2.35 %,
Temperature -20.0 °C
 17297 psi

@Strain 2.35 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
122.31 MPa

@Strain 2.20 %,
Temperature -20.0 °C
 17740 psi

@Strain 2.20 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
125.45 MPa

@Strain 2.39 %,
Temperature 0.000 °C
 18195 psi

@Strain 2.39 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
130.93 MPa

@Strain 2.89 %,
Temperature 23.0 °C
 18990 psi

@Strain 2.89 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
134.96 MPa

@Strain 3.12 %,
Temperature -20.0 °C
 19574 psi

@Strain 3.12 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
140.72 MPa

@Strain 2.87 %,
Temperature 0.000 °C
 20410 psi

@Strain 2.87 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
141.08 MPa

@Strain 2.68 %,
Temperature -20.0 °C
 20462 psi

@Strain 2.68 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
156.08 MPa

@Strain 3.17 %,
Temperature -20.0 °C
 22638 psi

@Strain 3.17 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
161.7 MPa

@Strain 2.80 %,
Temperature -40.0 °C
 23460 psi

@Strain 2.80 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
Elongation at Break 4.0 %
4.0 %
DAM; ISO 527-1/-2
10 %
10 %
50%RH; ISO 527-1/-2
Tensile Modulus 3.50 GPa
508 ksi
50%RH; ISO 527-1/-2
6.00 GPa
870 ksi
DAM; ISO 527-1/-2
1.693 GPa

@Temperature 150 °C
 245.5 ksi

@Temperature 302 °F
 50%RH; ISO 11403-1 -2
1.988 GPa

@Temperature 150 °C
 288.3 ksi

@Temperature 302 °F
 DAM; ISO 11403-1 -2
2.427 GPa

@Temperature 60.0 °C
 352.0 ksi

@Temperature 140 °F
 50%RH; ISO 11403-1 -2
3.007 GPa

@Temperature 60.0 °C
 436.1 ksi

@Temperature 140 °F
 DAM; ISO 11403-1 -2
6.325 GPa

@Temperature -20.0 °C
 917.4 ksi

@Temperature -4.00 °F
 DAM; ISO 11403-1 -2
6.451 GPa

@Temperature -20.0 °C
 935.6 ksi

@Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
Flexural Modulus 5.00 GPa
725 ksi
DAM; ISO 178
Shear Modulus 0.407 GPa

@Temperature 160 °C
 59.0 ksi

@Temperature 320 °F
 DAM; Dynamic; ISO 11403-1 -2
0.429 GPa

@Temperature 120 °C
 62.2 ksi

@Temperature 248 °F
 DAM; Dynamic; ISO 11403-1 -2
0.537 GPa

@Temperature 70.0 °C
 77.9 ksi

@Temperature 158 °F
 DAM; Dynamic; ISO 11403-1 -2
Users viewing this material also viewed the following: