SABIC Innovative Plastics LNP LUBRICOMP RFP36S PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RFP36S PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RFP36S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Wear Resistant, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.700 % | 0.700 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0021 cm/cm @Time 86400 sec |
0.0021 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0097 cm/cm @Time 86400 sec |
0.0097 in/in @Time 24.0 hour |
ISO 294 |
| 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 133 MPa | 19300 psi | ASTM D638 |
| 135 MPa | 19600 psi | ISO 527 | |
| Elongation at Break | 2.1 % | 2.1 % | ASTM D638 |
| 2.2 % | 2.2 % | ISO 527 | |
| Tensile Modulus | 9.80 GPa | 1420 ksi | 1 mm/min; ISO 527 |
| 10.48 GPa | 1520 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| 207 MPa | 30000 psi | ISO 178 | |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| 9.40 GPa | 1360 ksi | ISO 178 | |
| Izod Impact, Notched | 1.38 J/cm | 2.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.56 | 0.56 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.48 | 0.48 | ASTM D3702 Modified |
| K (wear) Factor | 22.2 x 10-8 mm³/N-M | 11.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 236 °C | 457 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 233 °C @Thickness 3.20 mm |
451 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Overview of materials for Acetal Copolymer, Aramid Fiber Filled
- Indium Corp. Indalloy 15 Low Melting Bismuth Alloy
- LATI Latishield 87/28-10A G/20 PC, Steel/Glass Fiber Reinforced
- Dalau Dalcon 025 75% Virgin PTFE, 25% Glass Fiber, Blue
- Tra-Con Tra-Duct 2916T Room Temperature Conductive Silver Epoxy Adhesive
- Cossa Polimeri ESTABLEND 4501 V0/D Flame Retardant PC - ABS
- DuPont Teijin Films Melinex® ST730 Polyester Film
- 3M 4296T Adhesion Promoter
- SABIC Innovative Plastics LNP Verton UV007S PPA (Asia Pacific)
- NOVA Chemicals Sclair® 2508-UV13 MDPE Injection Molding Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved