Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 120 MPa | 17400 psi | |
Plastcom SLOVAMID 6 GF 20 FRG 3 PA6, 20% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 20 % glass fibre, with halogen free flame retardant. Main features: flammability in accordance with UL 94 V2 at 1.6 mm, glow wire at 9.. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | STN EN ISO 527-2 |
Plastcom SLOVAMID® 66 GF 15 002 PA66 reinforced with glass fiber PA66 for injection molding, reinforced with 15 % glass fiber, for moldings used in the automotive, electrical, building, engineering and hobby industry - holders of electric hand tools, hobby tools,.. |
|||
Tensile Strength at Break | 120 MPa @Temperature 23.0 °C |
17400 psi @Temperature 73.4 °F |
ISO 527 |
Victrex® APTIV® 2102-050 Polyetheretherketone (PEEK) Polymer Film, Amorphous, Mineral Filled
(discontinued ** APTIV PEEK 2100 series films are the mineral filled amorphous films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.APTIV.. |
|||
Tensile Strength at Break | 120 MPa @Temperature 23.0 °C |
17400 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Sorona® FG3015G NC010 Polytrimethylene Terephthalate (PTT)
(Unverified Data** Sorona® FG3015G NC010 is a 15% glass fiber reinforced polytrimethylene terephthalate resin containing 31% renewably sourced ingredients by weight (37% based on polymer only) formulated to be food c.. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1/-2 |
Lanxess Durethan® BKV 15 G H2.0 900051 Copolyamide, 15% Glass Fiber CoPA, injection molding grade, 15% glass fibers, better surface resistance to alcoholic calcium chloride-solution than BKV 15 H2.0, good heat-ageing resistance |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1/-2 |
Lanxess Pocan® B 3225 000000 PBT, 20% Glass Fiber PBT, 20% glass fibers, injection molding |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1/-2 |
Lanxess Pocan® B 3225 901510 PBT, 20% Glass Fiber PBT, 20% glass fibers, injection molding |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | cond.; ISO 527-1, -2; 5 mm/min |
Lanxess Durethan® BKV 35 H3.0 000000 Nylon 6, Glass Fiber Reinforced PA 6, 35% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527-1,-2 |
Lanxess Pocan® KU 2-7241 000000 PBT, 25% Glass Fiber PBT, 25% glass fibers, injection molding, flame retardant, improved impact strengthInformation provided by LANXESS. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | |
LATI Latistat 66-06 G/30 PA66, 30% Glass Fiber Reinforced Dissipative product based on Polyamide 66 (PA66). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplas.. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527 |
Solvay TECHNYL® C 218L V30 PA6, 30% glass fiber, Eh 50 Description: TECHNYL C 218 L V30 is a polyamide 6 reinforced with 30% glass fiber and UV stabilized.Colors: it is marketed in the natural and black color.Available in: Latin America Main Properties:.. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DC10EPFR PC LNP* STAT-KON* Lexan_DC10EPFR is a compound based on Polycarbonate containing Carbon Fiber. Added features of this grade include: Exceptional Processing, Flame Retardant, Electrically Conductive. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DE004 PC (Asia Pacific) LNP STAT-KON* DE004 is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® 5031 PBT (Europe-Africa-Middle East) VALOX 5031 is a 30% glass reinforced PBT+PC blend with low warpage characteristics. Applications: appliance handles, automotive doorhandles. This grade is a 508 with reduced warpage. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP WF007 PBT LNP THERMOCOMP WF007 is a compound based on PBT resin containing 35% Glass Fiber. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-93 |
Wellman Wellamid® MRGF1737-GY1 Nylon 6, 30% Mineral/Glass Reinforced Metallic gray, heat stabilizedAll information provided by Wellman Engineered Resins. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | ASTM D638 |
Unitika RUN35-TA Light resistant PA6, Conditioned Light resistant and internalInformation provided by Unitika Ltd. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® LV-3 X ESD black PA12-GF30 Grilamid LV-3 X ESD black is an antistatic Polyamide 12 for injection molding with 30% glass fiber reinforcement. Main attributes are: antistatic with resistivity < 106 Ohmgood fuel and zinc chlorid.. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® LV-30H FWA black 9225 PA12-GF30 Product description: Grilamid LV-30H FWA black 9225 is a 30 % glass fiber reinforced, heat stabilized polyamide12 injection molding grade with the following special features: Stiffness combined with.. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® TSG-30 PA666-GF30 Product description: Grilon TSG-30 is a heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 30% glass fibers. Grilon TSG-30 has the following important properties: Excellent fl.. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® PLS 93G35DH1 BK261 Nylon 6
(Unverified Data**) 35% Glass Reinforced Heat Stabilized Polyamide 6 Zytel PLS93G35DH1 BK261 is a 35% glass reinforced PA6 using SHIELD Technology only from DuPont it provides exceptional welding resistanceInformation .. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527 |
Eurotec® Tecopet® PT74 GR20 BK002 DA PET, 20% glass fiber reinforced, high heat stabilized, black Information provided by Eurotec® |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1 |
Barlog Plastics KEBATRON L1065X3 PPS, linear, 65% glass fiber / mineral reinforced PPS-GF/MD 65Information provided by BARLOG plastics GmbH. |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | ASTM D638 |
Beijing Chemical Industry KAIFA® 301-G30RF PBT Resin 30% glass fiber reinforced, flame retardant, good toughness, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Tensile Strength at Break | 120 MPa | 17400 psi | After 7 days in boiling water |
Gharda Chemicals GAFONE™ 3430GF PES, Glass Fiber-Reinforced
(discontinued **) Glass fiber reinforced granules for injection molding. With lower viscosity for molding intricate cross sections.Characteristics: Very high rigidityGood dielectric propertiesHigh mechanical strengt.. |