LATI Latistat 66-06 G/30 PA66, 30% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | LATI |
| Trade Name | Latistat |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latistat 66-06 G/30 PA66, 30% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Dissipative product based on Polyamide 66 (PA66). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0035 - 0.0065 cm/cm | 0.0035 - 0.0065 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0105 cm/cm | 0.0070 - 0.0105 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | |
| Elongation at Break | 1.8 % | 1.8 % | |
| Tensile Modulus | 10.0 GPa | 1450 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| Vicat Softening Point | 255 °C @Load 5.00 kg |
491 °F @Load 11.0 lb |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 600000 ohm | 600000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 275 - 300 °C | 527 - 572 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Lucent Polymers GPP-310 Polypropylene, 10% Glass Fiber Reinforced, Chemically Coupled, Impact Modified
- SABIC Innovative Plastics NORYL NH7112 PPE+HIPS (Europe-Africa-Middle East)
- Borealis Borcell™ HE1105 High Density Polyethylene Compound for Gas Injection of Cellular Coaxial Cables
- UBE UBESTA® 3030U Nylon 12 (After Formic Acid (10%) for 500 hours)
- A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer
- Chevron Phillips MarFlex® HHM TR-258 Low Density Linear Polyethylene, Blown Film
- Eurostar Staramide PX08000 PA6, Impact Modified, Injection Molded
- ConocoPhillips Hydroclear® 10W-40 Super All Season and Super Motor Oil
Copyright © lookpolymers.com All Rights Reserved