- SABIC Innovative Plastics LNP STAT-KON DC10EPFR PC
SABIC Innovative Plastics LNP STAT-KON DC10EPFR PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DC10EPFR PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* Lexan_DC10EPFR is a compound based on Polycarbonate containing Carbon Fiber. Added features of this grade include: Exceptional Processing, Flame Retardant, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.110 % | 0.110 % | 50% RH, 24 hrs; ASTM D570 |
| 0.170 % | 0.170 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 118 MPa | 17100 psi | 5 mm/min; ISO 527 |
| 120 MPa | 17400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 |
| 2.6 % | 2.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 7.57 GPa | 1100 ksi | 1 mm/min; ISO 527 |
| 7.94 GPa | 1150 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 169 MPa | 24500 psi | ISO 178 |
| 173 MPa | 25100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 176 MPa | 25500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.80 GPa | 986 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.80 GPa | 986 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.46 J/cm | 10.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 23.0 J @Temperature 23.0 °C |
17.0 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 46.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
25.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.0 - 6.0 ohm | 2.0 - 6.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- PSM Industries Pacific Sintered Metals Bronze BT-126 Powdered Metal
- Materion Beryllium Copper Alloy 165 Rod and Bar; H (TD04) Temper; over 25.4 to 76 mm (UNS C17000)
- Haysite SDL® H400 Polyester Composite
- Polyram PlusTek RA353M8 Nylon 66, 40% Mineral Filled
- Polyram Polytron P40B07 Polypropylene, 40% Long Glass Fiber, UV Stabilized
- Zoltek Panex 35® Milled Carbon Fibers
- ExxonMobil Enable™ 20-10CE Metallocene Polyethylene Resin (Africa & Middle East Grade)
- Diamond Polymers ABS 3501 HF
- Axiall 9209 Rigid PVC, Molding
Copyright © lookpolymers.com All Rights Reserved