SABIC Innovative Plastics LNP THERMOCOMP WF007 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP WF007 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP WF007 is a compound based on PBT resin containing 35% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
| 121 MPa | 17500 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
| 121 MPa | 17500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 11.03 GPa | 1600 ksi | 1 mm/min; ISO 527 |
| 16.88 GPa | 2448 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 185 MPa | 26800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 185 MPa | 26800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 186 MPa | 27000 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 9.83 GPa | 1430 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.88 GPa | 1430 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.780 J/cm | 1.46 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.20 J/cm | 11.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 222 °C @Thickness 3.20 mm |
432 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GB 20 LS PA66, 20% glass beads, light stability
- EG100A Polyurethane-based Biomedical Elastomer
- Lushan PP+GF30%+4% PR-3 Maleic Anhydride Grafted Polypropylene
- Iran Petrochemical (PCC) EX 2 HF 7750 High Density Polyethylene
- SABIC Innovative Plastics Noryl PKN4766 PPE+PS (Asia Pacific)
- UBE UBEPOL BR15HL HIPS (n-DM =0.03 wt %)
- DuPont Performance Polymers Crastin® SO653 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)
- Armstrong A-34 Epoxy Adhesive
- Chevron Phillips Xtel® XK2140 Polyphenylene Sulfide Alloy (discontinued **)
Copyright © lookpolymers.com All Rights Reserved