| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 55.0 MPa | 7980 psi | 2 mm/min; ISO 178 |
| Polimeri Europa Edistir RT 461F Polystyrene High impact, heat resistant polystyrene with good stiffness. Recommended for improving the thermal performance of injection moulded technical parts which are submitted to high temperature in service.. |
|||
| Flexural Strength | 55.0 - 58.0 MPa | 7980 - 8410 psi | ASTM D790 |
| Proto3000 Accura® 25 Plastic Stereolithography (SLA) Prototyping Polymer Description: A high stiffness engineered nanocomposite that opens new applications for stereolithography users. Features: Look and feel of molded polypropyleneOutstanding feature resolution and accu.. |
|||
| Flexural Strength | 55.0 - 75.0 MPa | 7980 - 10900 psi | ASTM D790-03 |
| Proto3000 Objet Digital Materials™ DM_8505Gray25 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr.. |
|||
| Flexural Strength | 55.0 - 75.0 MPa | 7980 - 10900 psi | ASTM D790-03 |
| Proto3000 Objet Digital Materials™ DM_8505Gray35 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr.. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ISO 178 |
| Nilit FRIANYL A63 HS28 Nylon 6.6 for injection molding Nylon 6.6 for injection molding, maximum cold and dry impact resistance.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | at 5% strain; ASTM D790 |
| Shell Carilon® D26FX100 Polyketone, General-Purpose Extrusion Grade
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer D26FX100 is a general-purpose extrusion grade with mechanical properties that classify it as an eng.. |
|||
| Flexural Strength | <= 55.0 MPa | <= 7980 psi | ISO 178 |
| Polykemi AB POLYfill PPH S4030 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | 1.0 in/min; 0.125" thickness; ASTM D-790 |
| Chevron Phillips K-Resin® KR01BR SBC
(discontinued **) K-Resin® Styrene-Butadiene Copolymer (SBC)Applications:Molded boxes with integral hingesMedical devicesDisplaysToysMedia packagingFeatures:Good stiffnessGood toughnessGood warpage resistanceExcelle.. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | |
| Lehmann & Voss LUVOCOM® 65-8452-2 PP-copolymer, with carbon fiber, aramid reinforcement, lubricant modified Applications: Office communication.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Dynamic stressed parts.Information provided by.. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | |
| Lehmann & Voss LUVOCOM® 80-7695 Polyacetal-copolymer, with glass fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl.. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON WS002I PBT (Asia Pacific) LNP* Stat-kon* WS002I is a compound based on Polybutylene Terephalate resin containing Stainless Steel. Added features of this material include: Electrically Conductive, High Impact. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP STAT-LOY A3000 ABS (Europe-Africa-Middle East) LNP* Stat-loy* A3000 is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: Antistat. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS LNP* STAT-LOY* AF3009 is a compound based on ABS resin containing 10% Glass Fiber. Added features of this material include: Antistatic, Flame Retardant. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP HB006 PA11 LNP* Thermocomp* HB006 is a compound based on Nylon 11 resin containing 30% Glass Bead. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP MF001AS PP (Asia Pacific) LNP* Thermocomp* MF001AS is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP V1000UXC PA LNP* Thermotuf* V1000UXC is a compound based on Nylon resin. Added features of this material include: UV Stabilized. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Teknor Apex Sinpolene GPP5620 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Additive: Glass Fiber Reinforcement, 20% Filler by Weight Features: Good Dimensional Stability; High Heat Resistance; .. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| UBE UBESTA® 3014U Rigid Electronic Grade Nylon 12 Description: UBESTA Nylon 12 has an excellent termite resistance than other plastics. UBESTA contributes as a material for jacket and sheath which lay for telephone and telegram Communication System.. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Plenco 05118-T5 Phenolic, Granular, Compression Molded PLENCO 05118-T5 is a mineral and graphite filled novolac phenolic molding compound with PTFE, formulated for bearing seals. 05118 provides for a low coefficient of friction, good wear resistance, ve.. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Plenco 5118 Phenolic, Granular, Compression Molded PLENCO 05118 is a mineral and graphite filled phenolic molding compound, formulated for bearing seals. 05118 provides for a low coefficient of friction, abrasion resistance, minimal water absorptio.. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ISO 178-93 |
| Wellman Wellamid® XT1867-BK1 High Impact Nylon 66 Description: High Impact Nylon 66Information provided by Wellman. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| UBE UBESTA® 3030XA Nylon 12 Film Description: UBESTA Nylon 12 FilmInformation provided by UBE. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| UBE UBESTA® 3035UF Rigid Piping Grade Nylon 12 Description: UBESTA contributes to the field of Utilities such as plastic pipe system evolutionary developed for gas industry. It is used for both burial and for rehabilitation of existing cast iron.. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Polyram RamOfin PPC365T8 Polypropylene, 40% Mineral Filled 40% mineral filled, heat stabilized polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Ashley Polymers Ashlene® P261WO PPO A general purpose V-2 and V-0 rated resin for injection molding.Data provided by the manufacturer |
|||
| Flexural Strength | 55.0 - 58.0 MPa | 7980 - 8410 psi | ASTM D790 |
| 3D Systems Accura® 25 Plastic for SLA® Systems For use with solid-state stereolithography (SLA®) systems.ApplicationsFunctional components for assemblies and mock-ups for:Automotive styling parts — trim, fascia, and other componentsConsumer el.. |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | |
| Plastcom SLOVALEN PH 61 GB 30 PP, 30% glass beads, mod. of mech. prop. FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 30% glass beads, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP... |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ISO 178 |
| Unitika ET2025 PA6, Dry High-impact nylonInformation provided by Unitika Ltd. |
|||
| Flexural Strength | <= 55.0 MPa | <= 7980 psi | ISO 178 |
| Polykemi AB POLYfill PPH BF405510 VT1 Polypropylene Homopolymer, Reinforced, Heat Resistant Information provided by Polykemi AB |
|||
| Flexural Strength | 55.0 MPa | 7980 psi | ISO 178 |
| Grupo Repol Dinalon® B1X25 HI PA6 High Impact Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||