Plenco 5118 Phenolic, Granular, Compression Molded

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Mineral/Graphite Filled
Manufacturer Plenco (Plastics Engineering Company)
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plenco 5118 Phenolic, Granular, Compression Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PLENCO 05118 is a mineral and graphite filled phenolic molding compound, formulated for bearing seals. 05118 provides for a low coefficient of friction, abrasion resistance, minimal water absorption, and excellent dimensional stability under severe exposure. 05118 is available in gray. 05118 is not recommended for electrical insulating applications.Information supplied by Plenco.
Physical Properties Metric English Comments
Bulk Density 0.870 g/cc
0.0314 lb/in³
ASTM D1895
Density 1.81 g/cc
0.0654 lb/in³
ASTM D792
Water Absorption 0.044 %
0.044 %
ASTM D570
Linear Mold Shrinkage 0.00185 cm/cm
0.00185 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell E 59
59
ASTM D785
Tensile Strength, Ultimate 32.0 MPa
4640 psi
ASTM D638
Elongation at Break 0.40 %
0.40 %
ASTM D638
Tensile Modulus 11.7 GPa
1700 ksi
ASTM D638
Flexural Strength 55.0 MPa
7980 psi
ASTM D790
Flexural Modulus 10.0 GPa
1450 ksi
ASTM D790
Compressive Strength 134 MPa
19400 psi
ASTM D695
Izod Impact, Notched 0.156 J/cm
0.292 ft-lb/in
ASTM D256
Charpy Impact, Notched 0.176 J/cm²
0.838 ft-lb/in²
ASTM D256
Impact 57
57
J/m Drop Ball Impact; PLENCO
Thermal Properties Metric English Comments
CTE, linear 32.0 µm/m-°C

@Temperature 40.0 - 130 °C
17.8 µin/in-°F

@Temperature 104 - 266 °F
TMA; ASTM E831
Thermal Conductivity 1.22 W/m-K

@Temperature 100 °C
8.47 BTU-in/hr-ft²-°F

@Temperature 212 °F
ASTM E1461
Maximum Service Temperature, Air 211 °C
412 °F
Heat Resistance; ASTM D570D
Deflection Temperature at 1.8 MPa (264 psi) 193 °C
379 °F
ASTM D648
Oxygen Index 43 %
43 %
ASTM D2863
Shrinkage 0.057 %
0.057 %
72 hr, 120ºC; ASTM D1299