UBE UBESTA® 3035UF Rigid Piping Grade Nylon 12
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | UBE |
| Trade Name | UBESTA® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | UBE UBESTA® 3035UF Rigid Piping Grade Nylon 12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UBESTA contributes to the field of Utilities such as plastic pipe system evolutionary developed for gas industry. It is used for both burial and for rehabilitation of existing cast iron and steel gas mains. The excellent performance, especially creep and chemical resistance UBESTA supports industry as one of the most reliable materials.Comments: heat resistanceInformation provided by UBE.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ASTM D792 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength at Break | >= 54.0 MPa | >= 7830 psi | ASTM D638 |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | ASTM D638 |
| Elongation at Break | >= 250 % | >= 250 % | ASTM D638 |
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Flexural Modulus | 1.42 GPa | 206 ksi | ASTM D790 |
| Izod Impact, Notched | 0.780 J/cm | 1.46 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 178 °C | 352 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 230 °C | 446 °F | Flange Temperature for T-Die Cast Film Extrusion |
| Feed Temperature | 40.0 °C | 104 °F | Injection Molding |
| Zone 1 | 190 °C | 374 °F | For T-Die Cast Film Extrusion |
| 220 °C | 428 °F | Injection Molding | |
| 230 °C | 446 °F | For 8x1 mm Tube Extrusion | |
| Zone 2 | 210 °C | 410 °F | For T-Die Cast Film Extrusion |
| 225 °C | 437 °F | For 8x1 mm Tube Extrusion | |
| 230 °C | 446 °F | Injection Molding | |
| Zone 3 | 220 °C | 428 °F | For 8x1 mm Tube Extrusion |
| 230 °C | 446 °F | For T-Die Cast Film Extrusion | |
| 240 °C | 464 °F | Injection Molding | |
| Zone 4 | 215 °C | 419 °F | For 8x1 mm Tube Extrusion |
| 240 °C | 464 °F | Injection Molding | |
| Zone 5 | 230 °C | 446 °F | Injection Molding |
| Die Temperature | 230 °C | 446 °F | For T-Die Cast Film Extrusion |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Injection Velocity | 100 mm/sec | 3.94 in/sec | Injection Molding |
| Die Opening | 0.0400 cm | 0.0157 in | For T-Die Cast Film Extrusion |
| Roll Temperature | 50.0 °C | 122 °F | Chill Roll Temperature for T-Die Cast Film Extrusion |
| Drying Temperature | 80.0 °C | 176 °F | Option 1 |
| 100 °C | 212 °F | Option 2 | |
| 110 °C | 230 °F | Option 3 | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Option 3 |
| 4 - 6 hour | 4 - 6 hour | Option 2 | |
| 6 - 8 hour | 6 - 8 hour | Option 1 | |
| Injection Pressure | 40.0 - 50.0 MPa | 5800 - 7250 psi | Injection Molding (Injection pressure should be increased when molding thin wall parts. Pressure up to 75 bar can be used here.) |
| Hold Pressure | 25.0 - 50.0 MPa | 3630 - 7250 psi | Injection Molding |
| Back Pressure | 5.00 MPa | 725 psi | Injection Molding |
| Screw Speed | 15 - 76 rpm | 15 - 76 rpm | For 8x1 mm Tube Extrusion |
| Descriptive Properties | Value | Comments |
|---|---|---|
| C/R | 3-3.5:1 | For 8x1 mm Tube Extrusion |
| Calibrating Vacuum | 100 mbar | For 8x1 mm Tube Extrusion |
| Calibration | 9.95 mm | For 8x1 mm Tube Extrusion |
| Compression Ratio | 2.5-3.5:1 | Injection Molding |
| min 3:1 | For 8x1 mm Tube Extrusion | |
| Die Diameter | 16 mm | For 8x1 mm Tube Extrusion |
| Die Width | 300 mm | For T-Die Cast Film Extrusion |
| Extruder | Barmag, Screw Diameter = 30 mm | For T-Die Cast Film Extrusion |
| Extruder Characteristics | 65 mm screw diameter | For 8x1 mm Tube Extrusion |
| Film Thickness | 60 microns | For T-Die Cast Film Extrusion |
| Flight Depth in the Feeding Zone | 10-15% of Screw Diameter | Injection Molding |
| Flight Depth in the Metering Zone | 5-7% of Screw Diameter | Injection Molding |
| Haul Off Speed | 5 m/min | For T-Die Cast Film Extrusion |
| Haul Speed | 10-55 m/min | For 8x1 mm Tube Extrusion |
| L/D Ratio | 25:1 | For 8x1 mm Tube Extrusion |
| min 20:1 | Injection Molding | |
| Length of Compression Zone | 25-45% of total screw length | Injection Molding |
| 30% of screw length | For 8x1 mm Tube Extrusion | |
| Length of Feeding Zone | 20-40% of total screw length | Injection Molding |
| 30-40% of screw length | For 8x1 mm Tube Extrusion | |
| Length of Metering Zone | 30-45% of screw length | For 8x1 mm Tube Extrusion |
| 35-45% of total screw length | Injection Molding | |
| Mandrel Diameter | 12 mm | For 8x1 mm Tube Extrusion |
| Peripheral screw speed | 10 m/min | Injection Molding |
| Water Temperature | 10-18°C | For 8x1 mm Tube Extrusion |
Users viewing this material also viewed the following:
- MV Labs MG100 Mg(C2H3O2)2·4H2O Magnesium acetate tetrahydrate
- SABIC Innovative Plastics Cycolac® INP222 ABS
- Pyrotek F-24 Dense Machinable Board
- Kazanorgsintez Oxanol CS-100
- Solvay TECHNYL® A 402 Natural FA PA66, Conditioned
- A. Schulman POLYBATCH™ White 8153/UV2 Concentrate Based In Polyethylene
- A. Schulman PP 3369-01 Polypropylene Medium-Flow Homopolymer Polypropylene
- EMS-Griltech Grilon® XC 145 Nylon 6 Monofilament (Non-Set)
- Ensinger XP-132 Compression Molded PI Compound, 15% Graphite Filled
- Eurostar Starflam RF023P PA66/6, Glass Fiber Filled, Flame Retardant, Injection Molded
Copyright © lookpolymers.com All Rights Reserved