Lehmann & Voss LUVOCOM® 65-8452-2 PP-copolymer, with carbon fiber, aramid reinforcement, lubricant modified
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 65-8452-2 PP-copolymer, with carbon fiber, aramid reinforcement, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Office communication.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Dynamic stressed parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 40.0 MPa | 5800 psi | |
| Elongation at Yield | 6.0 % | 6.0 % | |
| 8.0 % | 8.0 % | flexural | |
| Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
| Flexural Strength | 55.0 MPa | 7980 psi | |
| Flexural Modulus | 6.00 GPa | 870 ksi | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 130 °C | 266 °F | short term | |
| Vicat Softening Point | 80.0 °C | 176 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm | |
| Insulation Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 230 - 260 °C | 446 - 500 °F | mass temp |
| Nozzle Temperature | 220 - 250 °C | 428 - 482 °F | |
| Zone 1 | 220 - 250 °C | 428 - 482 °F | |
| Zone 2 | 220 - 250 °C | 428 - 482 °F | |
| Zone 3 | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 70.0 - 95.0 °C @Time 7200 - 14400 sec |
158 - 203 °F @Time 2.00 - 4.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | graphite grey |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 NG GF 45 PA6, 45% glass fibre
- Quadrant EPP Semitron® ESd 500HR PTFE, static dissipative, extruded (ISO Data)
- PolyOne Edgetek® AS-03CF/000 Acrylonitrile Butadiene Styrene (ABS), Carbon Fiber Reinforced (discontinued **)
- Lehmann & Voss LUVOCOM® 80-7626 Polyacetal-copolymer, with carbon fiber
- A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66
- EMS-Grivory Grivory® GVL-6H black 9839 PA*-GF60
- 3M 920XL Extended Liner Tapes
- Kleerdex Kydex® 115 Acrylic/PVC Thermoplastic Sheet (discontinued **)
- CENTROPLAST CENTROLYTE Polyethylene terephthalate
Copyright © lookpolymers.com All Rights Reserved