3D Systems Accura® 25 Plastic for SLA® Systems

Category	Polymer , Rapid Prototyping Polymer
Manufacturer	3D Systems Corporation
Trade Name	Accura®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3D Systems Accura® 25 Plastic for SLA® Systems.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

For use with solid-state stereolithography (SLA®) systems.ApplicationsFunctional components for assemblies and mock-ups for:Automotive styling parts — trim, fascia, and other componentsConsumer electronic componentsToysSnap fit assembliesMaster patterns for RTV/silicone moldingReplace CNC machining of polypropylene to produce short-run plastic partsSimulate injection molded partsConcept and marketing modelsFeaturesLook and feel of molded polypropyleneHigh flexibility with excellent shape retentionOutstanding feature resolution and accuracyHigh production speedFully developed and tested build stylesAll information provided by 3D Systems.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc @Temperature 25.0 °C	0.0408 lb/in³ @Temperature 77.0 °F	Liquid
	1.19 g/cc @Temperature 25.0 °C	0.0430 lb/in³ @Temperature 77.0 °F	Solid
Viscosity	250 cP @Temperature 30.0 °C	250 cP @Temperature 86.0 °F

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	80	80
Tensile Strength, Yield	38.0 MPa	5510 psi	ASTM D638
Elongation at Break	13 - 20 %	13 - 20 %	ASTM D638
Tensile Modulus	1.59 - 1.66 GPa	231 - 241 ksi	ASTM D638
Flexural Strength	55.0 - 58.0 MPa	7980 - 8410 psi	ASTM D790
Flexural Modulus	1.38 - 1.66 GPa	200 - 241 ksi
Izod Impact, Notched	0.190 - 0.240 J/cm	0.356 - 0.450 ft-lb/in	ASTM D256
Penetration	4.2	4.2	mils

Thermal Properties	Metric	English	Comments
CTE, linear	107 µm/m-°C @Temperature 0.000 - 20.0 °C	59.4 µin/in-°F @Temperature 32.0 - 68.0 °F	T<Tg; ASTM E831-93
	151 µm/m-°C @Temperature 90.0 - 150 °C	83.9 µin/in-°F @Temperature 194 - 302 °F	T>Tg; ASTM E831-93
Deflection Temperature at 0.46 MPa (66 psi)	58.0 - 63.0 °C	136 - 145 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	51.0 - 55.0 °C	124 - 131 °F	ASTM D648
Glass Transition Temp, Tg	60.0 °C	140 °F	DMA, E"

Descriptive Properties	Value	Comments
Appearance	White
Critical Exposure (mJ/cm²)	10.5
Tested Build Styles	FAST™, EXACT™, Exact HR

Users viewing this material also viewed the following: