- Polymer Property : Flexural Strength = 75.0 MPa
Polymer Property : Flexural Strength = 75.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 |
| Polimeri Europa Edistir N 2560 Polystyrene High molecular weight general purpose polystyrene with good mechanical strength and good thermal resistance. It is recommended for in-line forming of disposable packaging, for sheet
extrusion in ble.. |
|||
| Flexural Strength | 75.0 - 110 MPa | 10900 - 16000 psi | ASTM D790-03 |
| Proto3000 Objet VeroBlack FullCure870 Rigid Opaque Prototyping Polymer Objet’s FullCure® Materials family of proprietary acrylic-based photopolymer materials enables Objet users to create highly accurate, finely detailed 3D models and parts for a wide range of Rapid .. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | 10mm/min; DIN 53452 |
| Qualchem Danamid FES-23 HUV Polyamide 6 Impact resistant, cold. Heat and UV stabilized, for long-lasting use at 120-130°C, protected against artificial light.Information provided by Qualchem Zrt. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | 10mm/min; DIN 53452 |
| Qualchem Danamid FES-23 Polyamide 6 Impact resistant, coldInformation provided by Qualchem Zrt. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP FARADEX AS003 ABS (Europe-Africa-Middle East) LNP* Faradex* AS003 is a compound based on Acrylonitrile Butadiene Styrene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP KONDUIT PX10322 PA 6 (Asia Pacific) Thermally conductive mineral filled PA6 FR compound, with through-plane and in-plane thermal conductivity of 1.7 W/(m*K) and 4.7 W/(m*K) respectively, conforming to ASTM E 1461 test standard. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP BX05029 SAN (Europe-Africa-Middle East) LNP* Lubricomp* BX05029 is a compound based on Styrene Acrylonitrile resin containing Mineral, Graphite. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | |
| Lehmann & Voss LUVOCOM® 6-7833 Polyamide 12, with PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Dynamic stressed parts.Low waterabsorbtion, for dimensional stable precision parts.Isotropic sh.. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | |
| Lehmann & Voss LUVOCOM® 6-7834 Polyamide 12, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Dynamic stressed parts.Low waterabsorbtion, for dimensional stable precision parts.Isotropic sh.. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | 2mm/min; ASTM D790 |
| Kingfa MAC-601 UV PC/ABS Alloy Features:Excellent balance propertiesHigh impact strengthGood processing propertiesApplications:Injection moldingAutomobile instrument panelElectrical and electronic partsComputer and accessoriesHou.. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | ISO 178 |
| Lucite International Diakon® ST25G6 Toughened Acrylic Polymer The Diakon® impact PMMA series offer the best combination of impact, chemical and heat resistance and provide rigidity and surface hardness. The grades in the Diakon® series can be processed b.. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | |
| Lehmann & Voss LUVOCOM® 1105-7583 PEEK, with glass fiber and PTFE, improved wear resistance Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Good friction and wear behaviour especially at increased temperatures.Chemical and hydroly.. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | 2mm/min; 80x10x4mm; ISO 178 |
| SYNTHOS Krasten® 137 General Purpose Polystyrene Easy flow. Examples of Application:Injection moulding – cups and containers for the food industry, medical devices, drawing templates.Extrusion – coextrusion, high gloss surface.Synthos wa.. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Lubricomp KP004AXZ Acetal Homopoly LNP* Lubricomp* KP004AXZ is a compound based on Acetal Homopolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP.. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP KP004AXZ ACETAL HOMOPOLYMER LNP* LUBRICOMP* KP004AXZ is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP Lubricomp NL002 PC+ABS (Europe-Africa-Middle East) LNP* Lubricomp* PCAL4020S is a compound based on PC+ABS Blend resin containing PTFE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON DSL229 PC (Asia Pacific) LNP* Stat-kon* DSL229 is a compound based on Polycarbonate resin containing PTFE, Stainless Steel. Added features of this material include: Electrically Conductive, Internally Lubricated. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | ISO 178 |
| Styrolution Luran® S 757 G UV White 37019 ASA Description: Particularly easy flowing injection molding grade for difficult moldings with large flow path/wall thickness ratios.Information provided by STYROLUTION, which is a joint venture between.. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP MX88028 PP LNP* THERMOCOMP* MX88028 is a compound based on Polypropylene resin containing Proprietary Filler(s). |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP PH1100B PA 6 LNP* THERMOCOMP* PH1100B is a compound based on Nylon 6 resin. Added feature of this material is: High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | 1.3 mm/min; ASTM D790 |
| Styron MAGNUMâ„¢ 8391 Acrylonitrile Butadiene Styrene (ABS) Resin Overview: MAGNUMâ„¢ 8391 ABS combines an excellent glossy appearance with high flow and medium impact performance. The mass continuous process) ABS technology of Styron ensures an ABS resin that .. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| SABIC Innovative Plastics NORYL INT2002 PPE+HIPS (Asia Pacific) PPE/HIPS unfilled for auto interior |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP WBL36L PBT (Asia Pacific) LNP* Lubricomp* WBL36L is a compound based on Polybutylene Terephalate resin containing Glass Bead, PTFE. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp KB002 Acetal Copoly (Asia Pacific) LNP* Thermocomp* KB002 is a compound based on Acetal Copolymer resin containing Glass Bead.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP MF002S PP LNP* Thermocomp* MF002S is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | ISO 178 |
| Polyram RamLloy PZF101 PC/PBT Alloy, Chemical Resistance PC/PBT alloy for injection molding applications, low temperature and chemical resistance.Information provided by Polyram. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | ISO 178 |
| Polyram RamShine PV527 Acrylonitrile Butadiene Styrene, Flame Retardant Flame retardant ABS for injection molding applications.Information provided by Polyram. |
|||
| Flexural Strength | 75.0 - 79.0 MPa | 10900 - 11500 psi | ASTM D790 |
| 3D Systems Accura® Xtreme White 200 Plastic Ultra tough white plastic to replace CNC Machined polypropylene and ABS articles FeaturesExceptionally tough and durableUsed for challenging functional assembliesUsed for snap fit assembl.. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | |
| Lehmann & Voss LUVOCOM® 1301-8144 PPS, linear, with mineral filler Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Low waterabsorbtion.High continuous use and heat distortion temperature. Non flammable.High chemic.. |
|||
| Flexural Strength | 75.0 MPa | 10900 psi | 3.5%; ISO 178 |
| GEHR Plastics PPE Polyphenylene Ether
(discontinued **) Polyphenylenether belongs to the group of amorphous materials and can be used in temperatures ranging from -50°C to approximately 105°C. PPE exhibits a high impact strength, a low water absorption.. |
|||