- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- Polyram RamShine PV527 Acrylonitrile Butadiene Styrene, Flame Retardant
Polyram RamShine PV527 Acrylonitrile Butadiene Styrene, Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamShine PV527 Acrylonitrile Butadiene Styrene, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant ABS for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ISO 2577 |
| Melt Flow | 55 - 60 g/10 min @Load 10.0 kg, Temperature 220 °C |
55 - 60 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527 |
| Flexural Strength | 75.0 MPa | 10900 psi | ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 9.50 kJ/m² | 4.52 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| Glow Wire Test | 700 °C | 1290 °F | G.W.I.T.; IEC 60695 |
| 960 °C | 1760 °F | G.W.F.I.; IEC 60695 |
Users viewing this material also viewed the following:
- Plansee MT11 Molybdenum-Tantalum
- Polykemi AB POLYfill PP HBK15030 D Polypropylene, Multifiller High Gloss, Detergent Resistant
- NanoAmor 95%, OD/ID: 3-20/1-3 nm Aligned Multi-Walled Carbon Nanotubes
- Solvay TECHNYL® C 216 V40 PA6, 40% glass fiber, Conditioned
- Zircar Zirconia CeW-30 Ceria Woven Textile Insulation
- A. Schulman POLYBATCH™ Red 502 Concentrate Based In Polyethylene
- CP-Polymer-Technik Wellamid® 6600/50 GV 15 HWCP 15% Glass Fiber Nylon 66, Impact Modified Until 0°C, Heat Stabilized, Conditioned
- Entec Hylox® 9020 PBT, 20% Glass Reinforced
- Fainplast Compounds FR 86/2 Flexible PVC, Insulation
- Bhansali Engineering Abstron KU-600 ABS Super Heat Resistant
Copyright © lookpolymers.com All Rights Reserved