Qualchem Danamid FES-23 HUV Polyamide 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Qualchem Zrt. |
| Trade Name | Danamid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Qualchem Danamid FES-23 HUV Polyamide 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact resistant, cold. Heat and UV stabilized, for long-lasting use at 120-130°C, protected against artificial light.Information provided by Qualchem Zrt.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | DIN 53479 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527-1,2 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1,2 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ISO 527-1,2 |
| Flexural Strength | 75.0 MPa | 10900 psi | 10mm/min; DIN 53452 |
| Flexural Modulus | 1.80 GPa | 261 ksi | DIN 53452 |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | NB @Temperature -20.0 °C |
NB @Temperature -4.00 °F |
DIN 53453 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
DIN 53453 | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -20.0 °C |
7.14 ft-lb/in² @Temperature -4.00 °F |
DIN 53453 |
| 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB @Thickness 4.00 mm |
HB @Thickness 0.157 in |
MSZ 10383 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | DIN 53482 |
| Comparative Tracking Index | 525 V | 525 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | 3.0 - 3.2 % | 3.0 - 3.2 % | DIN 53714 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C4220K PC+ABS (Asia Pacific)
- Ravago Manufacturing Americas Hybrid S464LG Acrylonitrile Butadiene Styrene + PC Alloy
- 3M Dyneon™ PFA 6505N Perfluoroalkoxy Fluorothermoplastic (discontinued **)
- Kazanorgsintez P2KP Polyethylene Pigment Masterbatches
- SABIC Innovative Plastics PC1800R PC (Asia Pacific)
- Unitika E-RUNG60 Ultra high-rigidity PA6, Conditioned
- A. Schulman POLYBATCH™ Bright While LL80250 Concentrate Based In LLDPE
- Chevron Phillips MarFlex® D350 m-LLDPE Linear Low Density Polyethylene
- Arlon 49581X010 0.0105" (0.267 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved