SABIC Innovative Plastics LNP Lubricomp KP004AXZ Acetal Homopoly
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, PTFE-Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp KP004AXZ Acetal Homopoly.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* KP004AXZ is a compound based on Acetal Homopolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| 1.49 g/cc | 0.0538 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.021 cm/cm @Time 86400 sec |
0.021 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0214 cm/cm @Time 86400 sec |
0.0214 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0205 cm/cm @Time 86400 sec |
0.0205 in/in @Time 24.0 hour |
ISO 294 |
| 0.021 cm/cm @Time 86400 sec |
0.021 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ISO 527 |
| 50.0 MPa | 7250 psi | ASTM D 638 | |
| Elongation at Break | 10.5 % | 10.5 % | ISO 527 |
| 12.5 % | 12.5 % | ASTM D 638 | |
| Tensile Modulus | 2.20 GPa | 319 ksi | 50 mm/min; ASTM D 638 |
| 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D 790 |
| 77.0 MPa | 11200 psi | ISO 178 | |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D 790 |
| 2.80 GPa | 406 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm @Temperature 23.0 °C |
0.899 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.27 J/cm @Temperature 23.0 °C |
8.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² @Temperature 23.0 °C |
13.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.16 | 0.16 | ASTM D 3702 Modified |
| K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C @Thickness 3.20 mm |
325 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 99.0 °C @Thickness 3.20 mm |
210 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD/L: 40-60 nm/1-2 um Multi-Walled Carbon Nanotubes
- SABIC Innovative Plastics LNP LUBRICOMP DFP36 PC
- Lanxess Pocan® DP CF 2200 000000 PBT+PC
- Silberline Sparkle Silver® Premier 132AR
- PlastxWorld CEVIAN® E11 Inherently Static Dissipative ABS
- ExxonMobil 150 Mobil DTE PM Ashless
- A. Schulman INVISION™ VX-5065UI Soft Touch Polyolefin Thermoplastic
- BLUESTAR LXS 109 PPE-PS
- SABIC Innovative Plastics LNP STAT-KON MFD03 PP
Copyright © lookpolymers.com All Rights Reserved