SABIC Innovative Plastics NORYL INT2002 PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL INT2002 PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE/HIPS unfilled for auto interior
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 11.1 g/10 min @Load 10.0 kg, Temperature 250 °C |
11.1 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | SABIC - Japan Method |
| Elongation at Break | 80 % | 80 % | SABIC - Japan Method |
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | ASTM D790 |
| Izod Impact, Notched | 2.94 J/cm | 5.51 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PE 4133Q (33403) Medium Density Polyethylene
- Global GA-2850 High Density Polyethylene, Blow Molding Grade (discontinued **)
- Kolon KOPA® KN333HI2 High Impact Nylon 66
- DuPont™ Bynel® 4033 Anhydride Modified HDPE
- Cytec Thornel® P-120 2K Carbon Fiber, Pitch Precursor
- BASF Ultradur S 4090 G4 BK5110 20% Glass Filled PBT
- Goodfellow Iron 79/Boron 16/Silicon 5 Alloy
- ATI Allegheny Ludlum Altemp® 718 Nickel-Base Superalloy, Solution Treated plus Precipitation Heat Treated, UNS N07718
Copyright © lookpolymers.com All Rights Reserved