SABIC Innovative Plastics LNP STAT-KON DSL229 PC (Asia Pacific)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP STAT-KON
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP STAT-KON DSL229 PC (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Stat-kon* DSL229 is a compound based on Polycarbonate resin containing PTFE, Stainless Steel. Added features of this material include: Electrically Conductive, Internally Lubricated.

Physical Properties	Metric	English	Comments
Density	1.39 g/cc	0.0502 lb/inÂ³	ASTM D792
Linear Mold Shrinkage, Flow	0.0050 cm/cm @Time 86400 sec	0.0050 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	46.0 MPa	6670 psi	ASTM D638
Elongation at Break	4.6 %	4.6 %	ASTM D638
Tensile Modulus	2.45 GPa	355 ksi	50 mm/min; ASTM D638
Flexural Strength	75.0 MPa	10900 psi	ASTM D790
Flexural Modulus	2.57 GPa	373 ksi	ASTM D790
Izod Impact, Notched	0.640 J/cm	1.20 ft-lb/in	ASTM D256
Izod Impact, Unnotched	5.93 J/cm	11.1 ft-lb/in	ASTM D4812

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	120 Â°C @Thickness 3.20 mm	248 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	UL 94 by SABIC-IP

Electrical Properties	Metric	English	Comments
Surface Resistance	10 - 1.00e+6 ohm	10 - 1.00e+6 ohm	ASTM D257
	10 - 1.00e+6 ohm	10 - 1.00e+6 ohm	ROA; IEC 60093