Polymer Property : Modulus of Elasticity = 653 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	4.50 - 10.0 GPa @Temperature 60.0 - 150 °C	653 - 1450 ksi @Temperature 140 - 302 °F	Average value: 6.93 GPa Grade Count:1
Overview of materials for Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled". Specific grades with glass content between 45..
Modulus of Elasticity	4.50 - 34.5 GPa	653 - 5000 ksi	Average value: 17.2 GPa Grade Count:42
Overview of materials for Polyetherimide (PEI), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, Carbon Fiber Filled". Each property range of values reported is minimum and maximum valu..
Modulus of Elasticity	4.50 GPa	653 ksi	ASTM D638
Albis Plastics Polypropylene A 12 H-GK20/GF20 C , 20% Glass Bead/20% Glass Fiber (discontinued **) Semi-crystalline Polypropylene Homopolymer (PPHP)Characteristics: Chemically Coupled Fiber; Good Dimensional StabilityApplications: Appliances, Furniture, Cases, Packaging and NoveltiesProcessing: I..
Modulus of Elasticity	4.50 - 29.0 GPa	653 - 4200 ksi	Average value: 16.5 GPa Grade Count:8
Overview of materials for Thermoplastic Polyimide, Carbon Fiber This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyimide, Carbon Fiber". Each property range of values reported is minimum and maximum va..
Modulus of Elasticity	4.50 - 9.60 GPa	653 - 1390 ksi	Average value: 7.77 GPa Grade Count:3
Overview of materials for Phenolic/Rubber; Molded This property data is a summary of similar materials in the MatWeb database for the category "Phenolic/Rubber; Molded". Each property range of values reported is minimum and maximum values of approp..
Modulus of Elasticity	4.50 - 26.5 GPa	653 - 3840 ksi	Average value: 18.2 GPa Grade Count:34
Overview of materials for Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled". Each property range of values reported is mini..
Modulus of Elasticity	4.50 GPa	653 ksi
Lehmann & Voss LUVOCOMÂ® 1105-8264 PEEK, with CNT Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Electrically conductive, suitable for continuous discharging of statically generated elect..
Modulus of Elasticity	4.50 GPa	653 ksi
Lehmann & Voss LUVOCOMÂ® 1t-7503 Polyamide 6/6T, with PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri..
Modulus of Elasticity	4.50 GPa	653 ksi
Lehmann & Voss LUVOCOMÂ® 3-8266/BL Polyamide 6, unreinforced Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteristics.Reduce..
Modulus of Elasticity	4.50 GPa	653 ksi
Lehmann & Voss LUVOCOMÂ® 50-3019 Polycarbonate, with glass fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High dimensionally stable precision parts, even at elevated te..
Modulus of Elasticity	4.50 GPa	653 ksi
Lehmann & Voss LUVOCOMÂ® 50-7164/BL02 Polycarbonate, with glass fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Reduced moment of inertia compared with metal parts.Low warpag..
Modulus of Elasticity	4.50 GPa	653 ksi
Lehmann & Voss LUVOCOMÂ® PEEK CLASSIX 7994 PEEK, unreinforced Applications: medical engineeringEspecially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh chemical resistance parts, non flammable.Inherent flame resistance.S..
Modulus of Elasticity	4.50 GPa	653 ksi
Lehmann & Voss LUVOCOMÂ® 1100-7725 VP Polyether sulfone, with glass fiber, lubricant modified Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally sta..
Modulus of Elasticity	4.50 GPa	653 ksi
Lehmann & Voss LUVOCOMÂ® 1-7032-B Polyamide 66, with aramid reinforcement and PTFE, lubricant modified, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved wear behaviour, low warpage.Improved heat resistance.Control disks, cams, sliding elem..
Modulus of Elasticity	4.50 GPa	653 ksi
Lehmann & Voss LUVOCOMÂ® 19-7745 Polyamide 46, with PTFE, improved wear resistance Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Isotropic shrinkage characteristics.Good friction and wear behaviour especially at increased te..
Modulus of Elasticity	4.50 GPa	653 ksi	ISO 527-2
Tisan TISAKRIL® 15% Glass Fiber Reinforced ABS TISAKRIL has a wide area of application in automotive, electronics, computer, construction, and furniture industries. General Specifications include: High surface luminosityEasy processabilityDimens..
Modulus of Elasticity	4.50 GPa	653 ksi	ISO 527-2
Tisan TISESTER® 15% Glass Fiber Reinforced and Heat Stabilized Polybutylene Terephthalate TISESTER has a wide area of application in automotive, electric/electronics and durable goods industries. General Specifications include: Excellent surface appearanceHigh corrosion and abrasion resi..
Modulus of Elasticity	4.50 GPa	653 ksi	ISO 527-2
Tisan TISLAMID® 6 30% Mineral Reinforced Nylon 6 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec..
Modulus of Elasticity	4.50 GPa @Thickness >=1.50 mm	653 ksi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2
Elektro-Isola Etronax P EP Phenolic, Polyester Fabric Reinforcement, Light Yellow, Sheets Description: This material is exceptionally strong and tough. Very low water absorption and the lowest swelling in water. High resistance to chemicals, including SF6 gas. Applications: Can be used i..
Modulus of Elasticity	4.50 GPa	653 ksi	TD; ExxonMobil Method
ExxonMobil Metallyte™ 15MM288 OPP Film Product Description: A high barrier, non-sealable OPP film with one-side metalized and one-side treated. MM288 is designed for use as the center web of a triplex lamination. The treated surface offe..
Modulus of Elasticity	4.50 GPa	653 ksi	ISO 527-2
BASF Ultradur B 4300 G2 10% Glass Filled PBT Ultradur B4300 G2 is an easy flowing injection molding PBT with 10% glass fiber reinforcement for rigid, tough, and dimensionally stable parts.Applications: Program switches, thermostat parts, small..
Modulus of Elasticity	4.50 GPa	653 ksi	ISO 527-2
BASF Ultradur® S 4090 G2 10% Glass Filled PBT Description: Is a PBT + ASA, easy-flowing injection-molding grades with 10% glass fibers; for rigid, tough and dimensionally stable technical parts e. g. housings, consoles, contact carriers, covers..
Modulus of Elasticity	4.50 GPa	653 ksi	ISO 178
Addiplast Addilene H 420 K24 Polypropylene Homopolymer High densityInformation provided by Addiplast.
Modulus of Elasticity	4.50 GPa	653 ksi	ISO 527-1/-2
BASF Ultramid® A3XZG5 BK 23187 25% Glass Filled PA66 FR (Conditioned) Description: Impact-modified, 25% glass-fiber reinforced injection-molding grade with improved flame retardance and enhanced long-term stability. Flame retardant based on red phosphorus; for compone..
Modulus of Elasticity	4.50 - 9.00 GPa	653 - 1310 ksi	Average value: 6.20 GPa Grade Count:5
Overview of materials for Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled". Each property range of values reported is ..
Modulus of Elasticity	4.50 - 8.50 GPa	653 - 1230 ksi	Average value: 6.81 GPa Grade Count:19
Overview of materials for Polyethylene Terephthalate (PET), 20% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 20% Glass Reinforced". Specific grades with glass content between 15% ..
Modulus of Elasticity	4.50 GPa	653 ksi
Lehmann & Voss LUVOCOM® 1301-8144 PPS, linear, with mineral filler Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Low waterabsorbtion.High continuous use and heat distortion temperature. Non flammable.High chemic..
Modulus of Elasticity	4.50 GPa	653 ksi
Lehmann & Voss LUVOCOM® 1700-7903 PPO, with glass fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance r..
Modulus of Elasticity	4.50 - 11.6521 GPa @Temperature -40.0 - 100 °C	653 - 1690.03 ksi @Temperature -40.0 - 212 °F	Average value: 6.55 GPa Grade Count:17
Overview of materials for Polypropylene with 40% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Glass Fiber Filler". Specific grades with glass content between 35% and 44% are i..