Overview of materials for Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Overview of materials for Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.

Physical Properties	Metric	English	Comments
Density	1.14 - 1.26 g/cc	0.0412 - 0.0455 lb/in³	Average value: 1.20 g/cc Grade Count:5
Water Absorption	0.300 - 0.400 %	0.300 - 0.400 %	Average value: 0.340 % Grade Count:5
Moisture Absorption at Equilibrium	0.100 - 0.150 %	0.100 - 0.150 %	Average value: 0.120 % Grade Count:5
Linear Mold Shrinkage	0.00300 - 0.00450 cm/cm	0.00300 - 0.00450 in/in	Average value: 0.00400 cm/cm Grade Count:5
Melt Flow	7.00 - 24.0 g/10 min	7.00 - 24.0 g/10 min	Average value: 14.6 g/10 min Grade Count:5

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	75.0 - 110 MPa	10900 - 16000 psi	Average value: 88.0 MPa Grade Count:5
Elongation at Break	2.50 - 4.00 %	2.50 - 4.00 %	Average value: 3.30 % Grade Count:5
Modulus of Elasticity	4.50 - 9.00 GPa	653 - 1310 ksi	Average value: 6.20 GPa Grade Count:5
Charpy Impact Unnotched	3.50 - 4.00 J/cm²	16.7 - 19.0 ft-lb/in²	Average value: 3.90 J/cm² Grade Count:5
	3.50 - 4.00 J/cm² @Temperature -30.0 - -30.0 °C	16.7 - 19.0 ft-lb/in² @Temperature -22.0 - -22.0 °F	Average value: 3.90 J/cm² Grade Count:5
Charpy Impact, Notched	1.10 - 1.40 J/cm²	5.24 - 6.66 ft-lb/in²	Average value: 1.24 J/cm² Grade Count:5
	1.10 - 1.40 J/cm² @Temperature -30.0 - -30.0 °C	5.24 - 6.66 ft-lb/in² @Temperature -22.0 - -22.0 °F	Average value: 1.24 J/cm² Grade Count:5
Tensile Creep Modulus, 1000 hours	2800 - 6100 MPa	406000 - 885000 psi	Average value: 4680 MPa Grade Count:3

Thermal Properties	Metric	English	Comments
CTE, linear	35.0 - 55.0 µm/m-°C	19.4 - 30.6 µin/in-°F	Average value: 43.0 µm/m-°C Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi)	136 - 145 °C	277 - 293 °F	Average value: 140 °C Grade Count:5
Deflection Temperature at 1.8 MPa (264 psi)	128 - 141 °C	262 - 286 °F	Average value: 135 °C Grade Count:5
Vicat Softening Point	138 - 145 °C	280 - 293 °F	Average value: 141 °C Grade Count:5
Flammability, UL94	HB - V-1	HB - V-1	Grade Count:5

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	Average value: 1.00e+15 ohm-cm Grade Count:5
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm	Average value: 1.00e+14 ohm Grade Count:5
Dielectric Constant	2.70 - 3.00	2.70 - 3.00	Average value: 2.87 Grade Count:5
Dielectric Strength	85.0 - 95.0 kV/mm	2160 - 2410 kV/in	Average value: 90.0 kV/mm Grade Count:5
Dissipation Factor	0.000800 - 0.00300	0.000800 - 0.00300	Average value: 0.00172 Grade Count:5
Comparative Tracking Index	225 - 250 V	225 - 250 V	Average value: 240 V Grade Count:5

Users viewing this material also viewed the following: