Lehmann & Voss LUVOCOM® 3-8266/BL Polyamide 6, unreinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 3-8266/BL Polyamide 6, unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteristics.Reduced moment of inertia compared with metal parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.69 g/cc | 1.69 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.011 - 0.015 cm/cm | 0.011 - 0.015 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 65.0 MPa | 9430 psi | |
| Elongation at Yield | 2.3 % | 2.3 % | |
| 3.0 % | 3.0 % | flexural | |
| Modulus of Elasticity | 4.50 GPa | 653 ksi | |
| Flexural Strength | 90.0 MPa | 13100 psi | |
| Flexural Modulus | 3.80 GPa | 551 ksi | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |
| 120 °C | 248 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | |
| Insulation Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 °C | 518 °F | mass temp |
| Nozzle Temperature | 270 - 280 °C | 518 - 536 °F | |
| Zone 1 | 250 - 270 °C | 482 - 518 °F | |
| Zone 2 | 270 - 290 °C | 518 - 554 °F | |
| Zone 3 | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 75.0 °C @Time 36000 - 57600 sec |
167 °F @Time 10.0 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | sapphire blue |
Users viewing this material also viewed the following:
- PTS Trimid® N66-G43HL 43% Glass Fiber Reinforced Heat Stabilized, Lubed Nylon 6/6
- M. Holland Company BS464 Specialty Polystyrene (discontinued **)
- SABIC Innovative Plastics Lexan® FL930 PC
- H.C. Starck Grade A Magnesium Diboride, MgB2
- Karina E 08/26-FC-LMP Beige Color Concentrate for PVC
- Lehmann & Voss LUVOCOM® 1105-7106 PEEK, with carbon fiber, PTFE, lubricant modified
- SABIC Innovative Plastics NORYL N850 PPE+PS
- Teknor Apex Monprene® MP-1393B Thermoplastic Elastomer
- Chevron Phillips Marlex® M250 Linear Low Density Polyethylene Black Concentrate
- Ametek Ultra 303L P/M Stainless Steel, Sintered from 6.0 g/cc Green Density
Copyright © lookpolymers.com All Rights Reserved