- Lehmann & Voss LUVOCOM® 1100-7725 VP Polyether sulfone, with glass fiber, lubricant modified
Lehmann & Voss LUVOCOM® 1100-7725 VP Polyether sulfone, with glass fiber, lubricant modified
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 10%Glass Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1100-7725 VP Polyether sulfone, with glass fiber, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Especially suitable for thin wall complex parts.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh quality terminal bar, switches and plugs, relais, lamp reflectors, sterilizable medical equipment.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 23.2 g/10 min @Load 5.00 kg, Temperature 345 °C |
23.2 g/10 min @Load 11.0 lb, Temperature 653 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 110 MPa | 16000 psi | |
| Elongation at Yield | 4.0 % | 4.0 % | |
| 4.5 % | 4.5 % | flexural | |
| Modulus of Elasticity | 4.50 GPa | 653 ksi | |
| Flexural Strength | 150 MPa | 21800 psi | |
| Flexural Modulus | 3.50 GPa | 508 ksi | |
| Charpy Impact Unnotched | 4.20 J/cm² | 20.0 ft-lb/in² | edgewise; ISO 179 1eU |
| Coefficient of Friction, Dynamic | 0.21 | 0.21 | |
| Coefficient of Friction, Static | 0.20 | 0.20 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 180 °C | 356 °F | |
| 200 °C | 392 °F | short term | |
| Vicat Softening Point | 215 °C | 419 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 350 °C | 662 °F | mass temp |
| Nozzle Temperature | 340 - 360 °C | 644 - 680 °F | |
| Zone 1 | 355 - 375 °C | 671 - 707 °F | |
| Zone 2 | 360 - 380 °C | 680 - 716 °F | |
| Zone 3 | 350 - 370 °C | 662 - 698 °F | |
| Mold Temperature | 120 - 200 °C | 248 - 392 °F | |
| Drying Temperature | 150 °C @Time 10800 - 18000 sec |
302 °F @Time 3.00 - 5.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (white) |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 41 UVT General Purpose Acrylic Resin
- Resin Technology Group Fusion 901 Odorless, Non-Frosting Fusion Cyanoacrylate
- Braskem ES 300 HDPE Blown Film Extrusion Polyethylene (discontinued **)
- Haynes Hastelloy® C-2000® Nickel Alloy Shielded Metal Arc Welded (SMAW) All Weld Cruciform
- Techmer ES HiFill FR® PA6 GF33 FR HS L 33% Glass Filled (Dry)
- Shinil Chemical SHINCON PPS-CF, Comp. "Y"-2 LCD Rack
- Covestro Desmopan® DP 3065D Polyurethane
- DuPont Performance Polymers Delrin® 525GR NC000 Acetal (POM) (Unverified Data**)
- ConocoPhillips Hydroclear® 10 Rolling Oil
- Multibase Multibatch® MP 52577 Sheet Extrusion