- Lehmann & Voss LUVOCOM® 50-3019 Polycarbonate, with glass fiber and PTFE
Lehmann & Voss LUVOCOM® 50-3019 Polycarbonate, with glass fiber and PTFE
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass + PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 50-3019 Polycarbonate, with glass fiber and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Improved friction and wear behaviour. Emergency running property.Strong, stiff parts.Body and duty parts in office equipment, gear wheels, grippers.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 80.0 MPa | 11600 psi | |
| Elongation at Yield | 3.5 % | 3.5 % | |
| 4.5 % | 4.5 % | flexural | |
| Modulus of Elasticity | 4.50 GPa | 653 ksi | |
| Flexural Strength | 120 MPa | 17400 psi | |
| Flexural Modulus | 3.50 GPa | 508 ksi | |
| Charpy Impact Unnotched | 3.90 J/cm² | 18.6 ft-lb/in² | flatwise; ISO 179 1fU |
| 3.70 J/cm² @Temperature -30.0 °C |
17.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179 1eA |
| Coefficient of Friction, Dynamic | 0.24 | 0.24 | |
| Coefficient of Friction, Static | 0.19 | 0.19 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C | 27.8 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 150 °C | 302 °F | short term | |
| Vicat Softening Point | 160 °C | 320 °F | DIN ISO 306 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 295 °C | 563 °F | mass temp |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Zone 1 | 280 - 300 °C | 536 - 572 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 300 - 320 °C | 572 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Halar® 6014 Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
- Spartech Plasticor Fluted PP Co/Pol Corrugated Sheet
- SABIC Innovative Plastics LNP STAT-KON SE003 PA 12 (Europe-Africa-Middle East)
- Samsung Cheil Industries Starex® TX-0510 TRABS, Unreinforced
- SMAC CABLE® 2519S-40-08 Damping Material
- Tra-Con Tra-Bond F253M Color Keyed High Temperature Epoxy Adhesive
- Tra-Con Tra-Bond Ablebond 724-1 Polyurethane Adhesive
- ExxonMobil HDPE AA48-002 High Density Polyethylene Resin
- Aclo Accuguard Polypropylene HPN469V2CSL Homopolymer Non-Halogenated Copper Stabilized
- DuPont Performance Polymers Neoprene AC MEDIUM Polychloroprene Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved