- Lehmann & Voss LUVOCOM® PEEK CLASSIX 7994 PEEK, unreinforced
Lehmann & Voss LUVOCOM® PEEK CLASSIX 7994 PEEK, unreinforced
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Unreinforced |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® PEEK CLASSIX 7994 PEEK, unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: medical engineeringEspecially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh chemical resistance parts, non flammable.Inherent flame resistance.Suitable for biocompatible application.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ISO 1183 |
| Water Absorption | <= 0.50 % | <= 0.50 % | 23°C/24h |
| Linear Mold Shrinkage | 0.010 - 0.016 cm/cm | 0.010 - 0.016 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 95.0 MPa | 13800 psi | |
| Elongation at Yield | 4.0 % | 4.0 % | |
| 6.0 % | 6.0 % | flexural | |
| Modulus of Elasticity | 4.50 GPa | 653 ksi | |
| Flexural Strength | 145 MPa | 21000 psi | |
| Flexural Modulus | 4.00 GPa | 580 ksi | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 260 °C | 500 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 190 °C | 338 - 374 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | beige red |
Users viewing this material also viewed the following:
- PolyOne Nymax™ GF 1200 A 33 HS Natural Polyamide 66 (Nylon 66)
- LG Chemical LI-921 ASA, Extrusion, High Stiffness
- Momentive Performance Materials Siloprenâ„¢ LSR 2750 Liquid Silicone Rubber - Self-Bonding
- Lucite International Diakon® CMH454L Acrylic Polymer
- Lucky EF-940 Acrylic, Injection/Extrusion Grade
- Indium Corp. Indalloy 53 Bismuth Solder Alloy
- Colorite Polymers 9812-10 Radiopaque Vinyl Compound
- Aremco Ceramabind™ 542 High Temperature Inorganic Binder
- Beijing Ranger Chem SM-828A90 Solvent Based Epoxy Resin
- Cheng Yu Plastic ML1230 PC/PTFE, 30% Glass
Copyright © lookpolymers.com All Rights Reserved