Tisan TISAKRIL® 15% Glass Fiber Reinforced ABS

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
Manufacturer	Tisan Engineering Plastics
Trade Name	TISAKRIL®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Tisan TISAKRIL® 15% Glass Fiber Reinforced ABS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

TISAKRIL has a wide area of application in automotive, electronics, computer, construction, and furniture industries. General Specifications include: High surface luminosityEasy processabilityDimensional stabilityInsulationLow weightHigh toughnessLow moisture absorptionHigh chemical resistance Glass fiber reinforced TISAKRIL increases mechanical resistance, surface hardness, melting point and specific gravity, while simultaneously reducing mold shrinkage. Calcite, talc, glass ball and other fillers may be used for reinforcement of TISAKRIL apart from glass fiber. It has excellent chemical resistance to weak acids, weak alkalis, and strong alkalis. It has good resistance against strong acids. It has weak chemical resistance against organic solvents, alcohols, hydrocarbons, and engine fuels.

Physical Properties	Metric	English	Comments
Density	1.10 g/cc	0.0397 lb/in³	ISO 1183
Linear Mold Shrinkage	0.0020 cm/cm	0.0020 in/in
Ash	15 %	15 %	ISO 3451

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	69.0 MPa	10000 psi	ISO 527-2
Tensile Strength, Yield	70.0 MPa	10200 psi	ISO 527-2
Elongation at Break	4.8 %	4.8 %	ISO 527-2
Elongation at Yield	5.0 %	5.0 %	ISO 527-2
Modulus of Elasticity	4.50 GPa	653 ksi	ISO 527-2
Izod Impact, Notched (ISO)	7.00 kJ/m²	3.33 ft-lb/in²	ISO 180

Thermal Properties	Metric	English	Comments
Melting Point	165 °C	329 °F
Vicat Softening Point	108 °C	226 °F	ISO 306
Heat Distortion Temperature	110 °C	230 °F	ISO 75-2
Flammability, UL94	HB	HB
Glow Wire Test	650 °C	1200 °F	60695-2-10

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	575 V	575 V	TS EN 60112

Processing Properties	Metric	English	Comments
Feed Temperature	60.0 °C	140 °F
Rear Barrel Temperature	190 - 210 °C	374 - 410 °F	Aft-1. Region Temperature
Middle Barrel Temperature	190 - 210 °C	374 - 410 °F	Mid-2. Region Temperature
Front Barrel Temperature	190 - 210 °C	374 - 410 °F	Pre-3. Region Temperature
Nozzle Temperature	200 °C	392 °F
Melt Temperature	160 - 180 °C	320 - 356 °F
Drying Temperature	80.0 °C	176 °F	Predrying Temperature
Dry Time	2 - 3 hour	2 - 3 hour	Predrying Time
Moisture Content	0.20 %	0.20 %	ISO 62

Descriptive Properties	Value	Comments
Block Temperature	45°C