Overview of materials for Phenolic/Rubber; Molded

Category Polymer , Thermoset , Phenolic , Phenolic/Rubber; Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Phenolic/Rubber; Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Phenolic/Rubber; Molded". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.34 - 1.60 g/cc
0.0484 - 0.0578 lb/in³
Average value: 1.51 g/cc Grade Count:3
Water Absorption 0.155 - 0.920 %
0.155 - 0.920 %
Average value: 0.413 % Grade Count:3
Linear Mold Shrinkage 0.00110 - 0.00790 cm/cm
0.00110 - 0.00790 in/in
Average value: 0.00378 cm/cm Grade Count:3
Mechanical Properties Metric English Comments
Hardness, Rockwell E 43.0 - 76.0
43.0 - 76.0
Average value: 54.3 Grade Count:3
Tensile Strength, Ultimate 34.0 - 74.0 MPa
4930 - 10700 psi
Average value: 54.7 MPa Grade Count:3
Elongation at Break 0.730 - 1.47 %
0.730 - 1.47 %
Average value: 0.983 % Grade Count:3
Modulus of Elasticity 4.50 - 9.60 GPa
653 - 1390 ksi
Average value: 7.77 GPa Grade Count:3
Flexural Yield Strength 56.0 - 115 MPa
8120 - 16700 psi
Average value: 87.0 MPa Grade Count:3
Flexural Modulus 3.60 - 8.90 GPa
522 - 1290 ksi
Average value: 6.97 GPa Grade Count:3
Compressive Yield Strength 82.0 - 157 MPa
11900 - 22800 psi
Average value: 118 MPa Grade Count:3
Izod Impact, Notched 0.233 - 0.470 J/cm
0.437 - 0.881 ft-lb/in
Average value: 0.364 J/cm Grade Count:3
Charpy Impact, Notched 0.281 - 0.450 J/cm²
1.34 - 2.14 ft-lb/in²
Average value: 0.357 J/cm² Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 53.0 - 53.0 µm/m-°C

@Temperature 40.0 - 130 °C
29.4 - 29.4 µin/in-°F

@Temperature 104 - 266 °F
Average value: 53.0 µm/m-°C Grade Count:1
Thermal Conductivity 0.440 - 0.440 W/m-K

@Temperature 100 - 100 °C
3.05 - 3.05 BTU-in/hr-ft²-°F

@Temperature 212 - 212 °F
Average value: 0.440 W/m-K Grade Count:1
Maximum Service Temperature, Air 92.0 - 244 °C
198 - 471 °F
Average value: 148 °C Grade Count:8
Deflection Temperature at 1.8 MPa (264 psi) 136 - 241 °C
277 - 466 °F
Average value: 203 °C Grade Count:3
Oxygen Index 24.6 - 37.0 %
24.6 - 37.0 %
Average value: 32.5 % Grade Count:3
Electrical Properties Metric English Comments
Electrical Resistivity 2.00e+11 - 6.40e+11 ohm-cm
2.00e+11 - 6.40e+11 ohm-cm
Average value: 4.87e+11 ohm-cm Grade Count:3
Dielectric Constant 4.50 - 5.80
4.50 - 5.80
Average value: 5.27 Grade Count:3
Dielectric Strength 10.5 - 13.2 kV/mm
267 - 335 kV/in
Average value: 12.0 kV/mm Grade Count:3
Dissipation Factor 0.0770 - 0.0830
0.0770 - 0.0830
Average value: 0.0803 Grade Count:3
Arc Resistance 67.0 - 135 sec
67.0 - 135 sec
Average value: 107 sec Grade Count:3
Comparative Tracking Index 150 - 175 V
150 - 175 V
Average value: 167 V Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 150 - 180 °C
302 - 356 °F
Average value: 166 °C Grade Count:5
Cure Time 0.583 - 3.00 min
0.00972 - 0.0500 hour
Average value: 1.63 min Grade Count:5