Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 7.00 - 9.00 GPa | 1020 - 1310 ksi | Injection; ISO 527 |
Raschig Group DECAL® 666/8/2B Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meets the allowe.. |
|||
Modulus of Elasticity | 7.00 - 9.00 GPa | 1020 - 1310 ksi | ISO 527 |
Raschig Group EN 5004 Epoxy Molding Compound Mica reinforced molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, outstanding heat resistance, very goo pourablity. This product meets the allowed upper limits fo.. |
|||
Modulus of Elasticity | 7.00 - 9.00 GPa | 1020 - 1310 ksi | ISO 527 |
Raschig Group EN 5007 Epoxy Molding Compound Mica reinforced molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, outstanding heat resistance, very goo pourablity. This product meets the allowed upper limits fo.. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 1105-8158 PEEK, with mineral filler Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precisio.. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 1105-8278/GY PEEK, with glass fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; impact resistance.Dynamic stressed parts at high movement velocity.Ch.. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 50-7289 Polycarbonate, with carbon fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Electrically conductive, suitable for cont.. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 65-8347/RD PP-copolymer, with carbon fiber Applications: Office communication.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Low warpage.Information provided by Lehmann & .. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 65-8452-2 PP-copolymer, with carbon fiber, aramid reinforcement, lubricant modified Applications: Office communication.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Dynamic stressed parts.Information provided by.. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 6-8395 Polyamide 12, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Especially suitable at dynamic stress situations.Electrically conductive, s.. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 80-7626 Polyacetal-copolymer, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Electrically conductive, suitable for continuous discharging of statically generated electricit.. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 80-7653 Polyacetal-copolymer, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Antistatic.No change of electric potential at bearings in case of separation of charge caused b.. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 80-8511 Polyacetal-copolymer, with carbon fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low warpage.High dimensionally.. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss ELECTRAFIL M-2386 Polycarbonate, with carbon fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Electrically conductive, suitable for cont.. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 1/GF/20/TF/10/SI/2/NC Polyamide 66, with glass fiber, PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Strong, stiff parts.Bearings, .. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 1104-8327 Polyether ketone, with glass fiber, easy flowing Applications: Automotive industry, mechanical- and precision engineering.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts.Low warpage.Information pro.. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 1105-8184 PEEK, with carbon fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Low warpage.Emergency running property.Information provided by Lehmann.. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 1200-7116-1 ABS, with carbon fiber Applications: Office communication.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Strong, stiff .. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 1/GF/20/TF/10/SI/2/BK Polyamide 66, with glass fiber, PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Strong, stiff parts.Bearings, .. |
|||
Modulus of Elasticity | 7.00 GPa @Thickness >=1.50 mm |
1020 ksi @Thickness >=0.0591 in |
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2 |
Elektro-Isola Etronax MF G Phenolic, Cotton Fabric Reinforcement, Black, Sheets Description: Exclusively for mechanical applications. Impact-resistant. Resistant to mechanical wear and noise-reducing. The graphite content causes low friction. Well suited for parts where there a.. |
|||
Modulus of Elasticity | 7.00 GPa @Thickness >=1.50 mm |
1020 ksi @Thickness >=0.0591 in |
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2 |
Elektro-Isola Etronax MMF Phenolic, Cotton Fabric Reinforcement, Brown, Sheets Description: Reinforced with a finer cotton fabric than Etronax MF. Also well suited in particular for small components which are subject to mechanical load and wear. Can be machined to finer tolera.. |
|||
Modulus of Elasticity | 7.00 GPa @Thickness >=1.50 mm |
1020 ksi @Thickness >=0.0591 in |
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2 |
Elektro-Isola Etronit IV C Phenolic, Paper Reinforcement, Yellow, Sheets Description: Grade for mechanical electrotechnical and high frequency purposes. Tropical grade, well suited for areas where high air humidity can be expected and lasting electrical properties despit.. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | ISO 527-2 |
BASF Ultraform® N2720 M63 30% Mineral Filled POM Description: Is a POM, 30 % mineral-reinforced material for low-warpage moldings with high stiffness, strength and hardness.Information provided by BASF |
|||
Modulus of Elasticity | 7.00 - 9.00 GPa @Temperature 70.0 - 70.0 °C |
1020 - 1310 ksi @Temperature 158 - 158 °F |
Average value: 5.80 GPa Grade Count:1 |
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Modulus of Elasticity | 7.00 - 9.00 GPa @Time 180000 - 1.44e+6 sec |
1020 - 1310 ksi @Time 50.0 - 400 hour |
Average value: 5.80 GPa Grade Count:1 |
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Modulus of Elasticity | 7.00 - 9.00 GPa | 1020 - 1310 ksi | Injection and Compression; ISO 527 |
Raschig Group RESINOL® 400 EPF Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and very good mechanical properties. This product meets .. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | ISO 178 |
Addiplast Addinyl B2H M30 Flame Retardant Nylon 6, 30% Mineral Filled Flame retardant, 30% mineral filled, with halogensInformation provided by Addiplast. |
|||
Modulus of Elasticity | 7.00 - 9.00 GPa @Temperature 60.0 - 160 °C |
1020 - 1310 ksi @Temperature 140 - 320 °F |
Average value: 7.94 GPa Grade Count:2 |
Overview of materials for Polysulfone, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are inc.. |
|||
Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 1105-7107/BK PEEK, with glass fiber, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precisio.. |