Lehmann & Voss LUVOCOM® 6-8395 Polyamide 12, with carbon fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 6-8395 Polyamide 12, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Especially suitable at dynamic stress situations.Electrically conductive, suitable for continuous discharging of statically generated electricity.Low waterabsorbtion, for dimensional stable precision parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0050 cm/cm | 0.0010 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 90.0 MPa | 13100 psi | |
| Elongation at Yield | 7.0 % | 7.0 % | |
| 9.0 % | 9.0 % | flexural | |
| Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
| Flexural Strength | 140 MPa | 20300 psi | |
| Flexural Modulus | 6.00 GPa | 870 ksi | |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| 140 °C | 284 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 100 ohm | <= 100 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | mass temp |
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |
| Zone 1 | 230 - 250 °C | 446 - 482 °F | |
| Zone 2 | 240 - 260 °C | 464 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 36000 sec |
167 °F @Time 6.00 - 10.0 hour |
Dehumidifying dryer |
| 105 °C @Time <=14400 sec |
221 °F @Time <=4.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- MV Labs AS850 (NH4)3AsO4 Ammonium arsenate tribasic
- Protective Coating PC-Concrete™ Epoxy Concrete Anchoring and Repair System
- PolyOne Edgetek® ATH-10CF/000 Acetal-Homopolymer, Carbon Fiber Reinforced (discontinued **)
- Northstar Polymers MPP-A80E High Performance Polyether
- Karina 850-10/116-Y-ERYB-AS White PVC Compound
- Heatbath/Park Parcure 300 Rubber Cure Salt
- A. Schulman POLYFORT™ FPP 1245U CaCO3 Filled UV Stable Copolymer Polypropylene
- Chesterton 995 Release Agent
- BASF Ultramid® SEGM35 H1 BK-126 15/25% Glass/Mineral Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved