BASF Ultraform® N2720 M63 30% Mineral Filled POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Mineral Filled
Manufacturer BASF
Trade Name Ultraform®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultraform® N2720 M63 30% Mineral Filled POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Is a POM, 30 % mineral-reinforced material for low-warpage moldings with high stiffness, strength and hardness.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.650 - 0.900 g/cc
0.0235 - 0.0325 lb/in³
Density 1.65 g/cc
0.0596 lb/in³
ISO 1183
Water Absorption 0.90 %
0.90 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 0.15 %
0.15 %
23°C; 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.012 cm/cm
0.012 in/in
ISO 2577
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
ISO 2577
Melt Flow 6.27 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 6.27 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 190 MPa

@Load 98.0 kg,
Time 30.0 sec
 27600 psi

@Load 216 lb,
Time 0.00833 hour
 ISO 2039-1
Tensile Strength, Yield 75.0 MPa
10900 psi
50 mm/min; ISO 527-2
Elongation at Break 6.0 %
6.0 %
Nominal, 50mm/min; ISO 527-2
Elongation at Yield 5.0 %
5.0 %
ISO 527-2
Modulus of Elasticity 7.00 GPa
1020 ksi
ISO 527-2
Izod Impact, Notched (ISO) 3.50 kJ/m²

@Temperature -30.0 °C
 1.67 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/A
3.50 kJ/m²

@Temperature 23.0 °C
 1.67 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/A
Charpy Impact Unnotched 5.50 J/cm²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
5.50 J/cm²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.300 J/cm²

@Temperature -30.0 °C
 1.43 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
0.350 J/cm²

@Temperature 23.0 °C
 1.67 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Tensile Creep Modulus, 1000 hours 2750 MPa

@Strain <=0.500 %
 399000 psi

@Strain <=0.500 %
 ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 45.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 25.0 µin/in-°F

@Temperature 73.4 - 131 °F
 DIN 53752
Melting Point 166 °C
331 °F
DIN 53765
Maximum Service Temperature, Air 110 °C
230 °F
Deflection Temperature at 1.8 MPa (264 psi) 140 °C
284 °F
ISO 75-2
Vicat Softening Point 155 °C
311 °F
ISO 306
Decomposition Temperature >= 240 °C
>= 464 °F
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 60093
Dielectric Constant 4.0

@Frequency 100 Hz
 4.0

@Frequency 100 Hz
 IEC 60250
4.2

@Frequency 1.00e+6 Hz
 4.2

@Frequency 1.00e+6 Hz
 IEC 60250
Dielectric Strength 43.0 kV/mm
1090 kV/in
IEC 60243-1
Dissipation Factor 0.0050

@Frequency 1.00e+6 Hz
 0.0050

@Frequency 1.00e+6 Hz
 IEC 60250
0.0070

@Frequency 100 Hz
 0.0070

@Frequency 100 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
Test solution A; IEC 60112
600 V
600 V
Test solution B; IEC 60112
Processing Properties Metric English Comments
Processing Temperature 200 °C
392 °F
Hopper Throat
Zone 1 205 °C
401 °F
Feed zone
Zone 2 205 °C
401 °F
Compression
Zone 3 210 °C
410 °F
Metering-zone
Zone 4 210 °C
410 °F
Nozzle
Melt Temperature 190 - 230 °C
374 - 446 °F
Injection-molding
210 °C
410 °F
Optimal
Mold Temperature 60.0 - 120 °C
140 - 248 °F
Injection-molding
100 °C
212 °F
Optimal
Drying Temperature 100 °C
212 °F
Dry Time 3 hour
3 hour
Descriptive Properties Value Comments
Commercial Status Europe
Ignition Temperature 320 - 340°C
ASTM D1929
Peripheral screw speed <0.3 m/s
Primary Processing Technique Injection Molding