Elektro-Isola Etronax MF G Phenolic, Cotton Fabric Reinforcement, Black, Sheets

Category	Polymer , Thermoset , Phenolic
Manufacturer	Elektro-Isola
Trade Name	Etronax
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Elektro-Isola Etronax MF G Phenolic, Cotton Fabric Reinforcement, Black, Sheets.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Exclusively for mechanical applications. Impact-resistant. Resistant to mechanical wear and noise-reducing. The graphite content causes low friction. Well suited for parts where there are high mechanical load and wear requirements. Good wear resistance in aggressive and dust-filled environments. Can be lubricated with water, oil or grease. Alternative to materials containing asbestos.Information provided by Elektro-Isola

Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/in³	24hr/23°C/50% RH; ISO 1183-A; IEC/EN 60893-2 8.1
Water Absorption	1.6 %	1.6 %	24hr/50°C+24hr in water at 23°C,Test Specimen 50x50x3[mm]; ISO 62-1; IEC/EN 60893-2 8.2

Mechanical Properties	Metric	English	Comments
Tensile Strength	80.0 MPa @Thickness >=1.50 mm	11600 psi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6
Modulus of Elasticity	7.00 GPa @Thickness >=1.50 mm	1020 ksi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2
Flexural Strength	135 MPa @Thickness >=1.50 mm	19600 psi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
Compressive Strength	330 MPa @Thickness >=5.00 mm	47900 psi @Thickness >=0.197 in	24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3
Shear Strength	50.0 MPa @Thickness >=5.00 mm	7250 psi @Thickness >=0.197 in	24hr/23°C/50% RH; IEC/EN 60893-2 5.5
Izod Impact, Notched (ISO)	10.0 kJ/m² @Thickness >=5.00 mm	4.76 ft-lb/in² @Thickness >=0.197 in	24hr/23°C/50% RH; ISO 180/2A; IEC/EN 60893-2 5.4.3

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Inert	100 °C @Thickness 0.000 mm, Time 7.20e+7 sec	212 °F @Thickness 0.000 in, Time 20000 hour	IEC 60216; IEC/EN 60893-2 7.1