- Lehmann & Voss LUVOCOM® 50-7289 Polycarbonate, with carbon fiber and PTFE
Lehmann & Voss LUVOCOM® 50-7289 Polycarbonate, with carbon fiber and PTFE
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 50-7289 Polycarbonate, with carbon fiber and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Improved friction and wear behaviour. Emergency running property.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Body and duty parts in office equipment, gear wheels, grippers.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | |
| Melt Flow | 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
9.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 95.0 MPa | 13800 psi | |
| Elongation at Yield | 2.5 % | 2.5 % | |
| 3.0 % | 3.0 % | flexural | |
| Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
| Flexural Strength | 140 MPa | 20300 psi | |
| Flexural Modulus | 6.00 GPa | 870 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 1eA |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | |
| Coefficient of Friction, Static | 0.20 | 0.20 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 150 °C | 302 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | |
| Vicat Softening Point | 160 °C | 320 °F | DIN ISO 306 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | |
| Insulation Resistance | <= 10000 ohm | <= 10000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 295 °C | 563 °F | mass temp |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Zone 1 | 280 - 300 °C | 536 - 572 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 300 - 320 °C | 572 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Kinetics MIM F75 (ASTM F75) HIP
- LATI Lastilac 11 G/10 ABS/PC, 10% Glass Fiber Reinforced
- Solvay Chemicals Barium carbonate granular
- Samsung Cheil Industries Starex® SR-0320 High Heat Resistant Grade ABS
- A. Schulman POLYBATCH™ Beige 1266E Concentrate Based In Polyethylene
- Dow LDPE 682I Low Density Polyethylene, Film Grade
- COI Ceramics Nicalon™ HI Type S SiC Ceramic Fiber
- BASF Ultradur B 4300 G6 BK5110 30% Glass Filled PBT
- Covestro Makrofol® LT 4-4 Polycarbonate
- SABIC Innovative Plastics LNP STAT-KON DX04490 PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved