- Lehmann & Voss LUVOCOM® 1104-8327 Polyether ketone, with glass fiber, easy flowing
Lehmann & Voss LUVOCOM® 1104-8327 Polyether ketone, with glass fiber, easy flowing
| Category | Polymer , Thermoplastic , Polyketone |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1104-8327 Polyether ketone, with glass fiber, easy flowing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, mechanical- and precision engineering.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts.Low warpage.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0050 - 0.010 cm/cm | 0.0050 - 0.010 in/in | |
| Melt Flow | 21.15 g/10 min @Load 10.0 kg, Temperature 380 °C |
21.15 g/10 min @Load 22.0 lb, Temperature 716 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 120 MPa | 17400 psi | |
| Elongation at Yield | 2.4 % | 2.4 % | |
| 3.0 % | 3.0 % | flexural | |
| Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
| Flexural Strength | 170 MPa | 24700 psi | |
| Flexural Modulus | 5.50 GPa | 798 ksi | |
| Charpy Impact Unnotched | 3.80 J/cm² | 18.1 ft-lb/in² | flatwise; ISO 179 1fU |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179 1eA |
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | |
| Coefficient of Friction, Static | 0.27 | 0.27 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | DIN 53752 |
| Maximum Service Temperature, Air | 255 °C | 491 °F | |
| 290 °C | 554 °F | short term | |
| Vicat Softening Point | >= 320 °C | >= 608 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Insulation Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 390 - 420 °C | 734 - 788 °F | |
| Zone 1 | 370 - 390 °C | 698 - 734 °F | |
| Zone 2 | 380 - 420 °C | 716 - 788 °F | |
| Zone 3 | 390 - 420 °C | 734 - 788 °F | |
| Mold Temperature | 180 - 230 °C | 356 - 446 °F | |
| Drying Temperature | 140 °C @Time 14400 - 57600 sec |
284 °F @Time 4.00 - 16.0 hour |
Dehumidifying dryer |
| 150 °C @Time 14400 - 28800 sec |
302 °F @Time 4.00 - 8.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® XHT1141 PC (Europe-Africa-Middle East)
- Mallard Creek Polymers Rovene® 4045 Styrene-Butadiene Emulsion
- Karina BR-11 White PVC Compound
- SABIC Innovative Plastics ULTEM HU1100 PEI
- Vyncolit Vyntec® CF8030 Carbon Fiber Reinforced Novolac Phenolic
- A. Schulman POLYFORT™ FPP 1842 Homopolymer Polypropylene
- Trelleborg B568 High Quality Nitrile Rubber
- Zircar Refractory Composites ASPA-970 Alumina-Silica Fiber Paper
- ChevronTexaco 5R Neutral Oil
- Caplinq LINQSTAT™ VCF-40810B
Copyright © lookpolymers.com All Rights Reserved