Polymer Resources PPX-G10 Modified-PPO, 10% Glass Reinforced
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 10% Glass Filled |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PPX-G10 Modified-PPO, 10% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Modified-Polyphenylene Oxide, 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 1.0 - 8.0 g/10 min @Load 11.6 kg, Temperature 250 °C |
1.0 - 8.0 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 104 | 104 | ASTM D785 |
| Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
| Tensile Strength, Yield | 72.4 MPa | 10500 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
| Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Temperature -30.0 °C |
1.50 ft-lb/in @Temperature -22.0 °F |
ASTM D256 |
| 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 260 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | ASTM D648 |
| Vicat Softening Point | 135 °C | 275 °F | 120°C/h, 50 N; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 304 °C | 500 - 580 °F | |
| Middle Barrel Temperature | 271 - 310 °C | 520 - 590 °F | |
| Front Barrel Temperature | 282 - 316 °C | 540 - 600 °F | |
| Melt Temperature | 288 - 316 °C | 550 - 600 °F | |
| Mold Temperature | 71.1 - 104 °C | 160 - 220 °F | |
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0015 |
Users viewing this material also viewed the following:
- PTS Tristar® PC-10R-(22) 22 MFI Polycarbonate With Release
- PTS Tristar® PC-10R-(VE) 12 MFI UV Stabilized Polycarbonate With Release
- PolyMirae Moplen HP500G Sheet and Thermoforming Grade Polypropylene
- Karina 810-37/3-CRB Ocher PVC Compound
- Momentive Performance Materials Silglaze® II Construction Sealant
- Techmer ES HiFill® PA6 GF15 IM BK 15% Glass Filled
- A. Schulman PP 3487-01 Polypropylene Homopolymer Polypropylene
- DSM Stanyl® TW271F8 (PA46+PTFE)-GF40
- ExxonMobil Vistalon™ 7500 Bimodal EPDM Polymer
- ExxonMobil Escorene™ AD 0633EH2 Ethylene Vinyl Acetate Copolymer (European Grade)
Copyright © lookpolymers.com All Rights Reserved