- Arkema Group Rilsan® ASR 30 Nylon 12, 30% Carbon Fiber Filled (Conditioned)
Arkema Group Rilsan® ASR 30 Nylon 12, 30% Carbon Fiber Filled (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Carbon Fiber Filled |
| Manufacturer | Arkema |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Rilsan® ASR 30 Nylon 12, 30% Carbon Fiber Filled (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Designation ISO 1874-PA12,M,16-120,CF30Rigid grade with carbon fiber filler (30%) for injection molding. Available color: black.Very high rigidity. High strength-to-weight ratio. Very low shrinkage: include 0,5% on average for the design of the mold. High dimensional stability (low moisture absorption). Antistatic properties.Example applications: Parts with high mechanical properties and dimensional precision.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 154 MPa | 22300 psi | 5 mm/min |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min |
| Tensile Modulus | 14.0 GPa | 2030 ksi | 1 mm/min |
| Charpy Impact Unnotched | 5.92 J/cm² | 28.2 ft-lb/in² | |
| 5.86 J/cm² @Temperature -30.0 °C |
27.9 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.55 J/cm² | 7.38 ft-lb/in² | |
| 0.910 J/cm² @Temperature -30.0 °C |
4.33 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature 20.0 °C |
22.2 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 174 °C | 345 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | |
| Vicat Softening Point | 170 °C | 338 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.10 mm |
HB @Thickness 0.122 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 400 ohm-cm | 400 ohm-cm | |
| Dielectric Strength | 1.00 kV/mm | 25.4 kV/in | |
| Comparative Tracking Index | 100 V | 100 V |
Users viewing this material also viewed the following:
- RheTech Products FRG220-773UB 20% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Flame Retardant, UV Stabilized, Light Grey
- SABIC Innovative Plastics LNP FARADEX DS0036I PC
- Nilit RECONYL B S20 Recycled nylon 6 for injection molding
- DSM Akulon® K224-PG2U (Cond.) 13% Glass Reinforced, Impact Modified Nylon 6 (North America) (discontinued **)
- Greene Tweed CHEMRAZ® 592 Perfluoroelastomer
- SABIC Innovative Plastics LNP LUBRICOMP DL003P PC (Asia Pacific)
- Skamol Group SKAMOLEX V-1100 (800) Customized Shape
- Formosa Plastics Formolon® 28 PVC
- Austin Novel Materials Texalan® 498A Polyester-based TPU
Copyright © lookpolymers.com All Rights Reserved