Supreme Petrochem SP 6460 High Heat Polystyrene

Category	Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Heat Resistant Grade
Manufacturer	Supreme Petrochem LTD
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Supreme Petrochem SP 6460 High Heat Polystyrene.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Characteristics High impact and modulus Easy flow High heat resistance & strength Available in any dark colorProcessing Injection moldingApplications Instrument enclosures Automobile interior parts Telecommunication components HVAC componentsMaterial Status: Commercial : ActiveAgency Ratings: Information provided by Supreme Petrochem LTD

Physical Properties	Metric	English	Comments
Specific Gravity	1.04 g/cc	1.04 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm	0.0040 - 0.0060 in/in	ASTM D792
Melt Flow	3.0 g/10 min @Load 10.0 kg, Temperature 200 Â°C	3.0 g/10 min @Load 22.0 lb, Temperature 392 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	49.0 MPa	7110 psi	50 mm/min; ASTM D638
Elongation at Break	50 %	50 %	50 mm/min; ASTM D638
Flexural Strength	78.5 MPa @Thickness 3.20 mm	11400 psi @Thickness 0.126 in	ASTM D790
Flexural Modulus	1.96 GPa @Thickness 3.20 mm	284 ksi @Thickness 0.126 in	ASTM D790
Izod Impact, Notched	1.30 J/cm @Thickness 3.20 mm	2.44 ft-lb/in @Thickness 0.126 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	120 Â°C	248 Â°F	ASTM D648
Vicat Softening Point	130 Â°C	266 Â°F	5kg / 120Â°C; ASTM D1525
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+16 ohm-cm	>= 1.00e+16 ohm-cm	IEC 93
Surface Resistance	>= 1.00e+14 ohm	>= 1.00e+14 ohm	IEC 93
Dielectric Constant	2.6 @Frequency 1e+6 Hz	2.6 @Frequency 1e+6 Hz	IEC 250
Dissipation Factor	0.00040 @Frequency 1e+6 Hz	0.00040 @Frequency 1e+6 Hz	IEC 250

Processing Properties	Metric	English	Comments
Melt Temperature	260 - 280 Â°C	500 - 536 Â°F
Mold Temperature	40.0 - 80.0 Â°C	104 - 176 Â°F
Drying Temperature	60.0 - 80.0 Â°C	140 - 176 Â°F	( 2 hrs) Pre drying temp.