Material Notes:

Rubber modified high impact polystyrene.Applications:Cosmetic packagingShower surroundsPoint of purchase displaysThin-wall injection molding and thermoformingFeatures:Smooth, glossy surface finishGood durabilityHigh impact and stiffnessExcellent toughnessInformation provided by Chevron PhillipsThe Chevron Phillips polystyrene product line was transferred to Americas Styrenics in 2008.

Physical Properties	Metric	English	Comments
Specific Gravity	1.03 g/cc	1.03 g/cc	ASTM D-792
Bulk Density	0.609 - 0.673 g/cc	0.0220 - 0.0243 lb/in³
Linear Mold Shrinkage	0.0040 - 0.0080 cm/cm	0.0040 - 0.0080 in/in	24 hours; ASTM D-955
Melt Flow	3.0 g/10 min @Load 5.00 kg, Temperature 200 °C	3.0 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D-1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	24.0 MPa	3480 psi	2.0 in/min; 0.050" thickness; ASTM D-638
Elongation at Yield	65 %	65 %	2.0 in/min; 0.050" thickness; ASTM D-638
Tensile Modulus	2.00 GPa	290 ksi	2.0 in/min; 0.050" thickness; ASTM D-638
Flexural Strength	39.0 MPa	5660 psi	0.1 in/min; 0.250" thickness; ASTM D-790B
Flexural Modulus	2.00 GPa	290 ksi	0.1 in/min; 0.250" thickness; ASTM D-790B
Izod Impact, Notched	1.28 J/cm @Thickness 3.17 mm, Temperature 22.8 °C	2.40 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F	ASTM D-256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	83.0 °C @Thickness 6.35 mm	181 °F @Thickness 0.250 in	ASTM D-648
Vicat Softening Point	99.0 °C @Thickness 6.35 mm	210 °F @Thickness 0.250 in	Rate B; ASTM D-1525