Polymer Property : Melt Flow = 12 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Flow 9.1 - 12 g/10 min

@Load 2.16 kg,
Temperature 230 °C
9.1 - 12 g/10 min

@Load 4.76 lb,
Temperature 446 °F
Procedure A; ASTM D1238
PolyOne Maxxam™ FR PP Concentrate 4 Polypropylene, Unspecified (PP, Unspecified)
Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V..
Melt Flow 2.0 - 12 g/10 min

@Load 5.00 kg,
Temperature 250 °C
2.0 - 12 g/10 min

@Load 11.0 lb,
Temperature 482 °F
ASTM D1238
Polymer Resources PC/ABS-G20 General Purpose PC/ABS Alloy, 20% Glass Filled
PC/ABS Alloy, General Purpose, 20% Glass FilledProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provi..
Melt Flow 5.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 265 °C
5.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 509 °F
ASTM D1238
Polymer Resources PC/TP-FR2 Flame Retardant PC/Polyester Alloy
Flame Retardant, High Impact, Excellent Chemical ResistanceFeatures: • Flame Retardant • Impact Modified • Self Extinguishing • Good Chemical ResistanceProcess: Injection MoldingNotes: All p..
Melt Flow 6.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 265 °C
6.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 509 °F
ASTM D1238
Polymer Resources PC/TP-GP2-[color]-UV PC/Polyester Alloy, UV-stabilized
High Impact, Excellent Chemical Resistance, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informa..
Melt Flow 6.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 265 °C
6.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 509 °F
ASTM D1238
Polymer Resources PC/TP-GP3-IM PC/Polyester Alloy, Impact Modified
Superior Chemical Resistance, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provide..
Melt Flow 5.0 - 12 g/10 min

@Load 1.20 kg,
Temperature 300 °C
5.0 - 12 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Polymer Resources PC-G10-[color]-1 Polycarbonate, 10% Glass Reinforced with Mold Release
Polycarbonate, 10% Glass Reinforced with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information..
Melt Flow 5.0 - 12 g/10 min

@Load 1.20 kg,
Temperature 300 °C
5.0 - 12 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Polymer Resources PC-G10-IM Polycarbonate, 10% Glass Reinforced, Impact Modified
Polycarbonate, 10% Glass Reinforced, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information ..
Melt Flow 3.0 - 12 g/10 min

@Load 1.20 kg,
Temperature 300 °C
3.0 - 12 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Polymer Resources PC-G30 Polycarbonate, 30% Glass Reinforced
Polycarbonate, 30% Glass ReinforcedFeatures: • Flame Retardant • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-p..
Melt Flow 3.0 - 12 g/10 min

@Load 1.20 kg,
Temperature 300 °C
3.0 - 12 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Polymer Resources PC-G30-TFE15 Polycarbonate, 30% Glass Reinforced, 15% PTFE
Polycarbonate, 30% Glass Reinforced, 15% PTFEProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provide..
Melt Flow 7.0 - 12 g/10 min
7.0 - 12 g/10 min
ASTM D1238
Polymer Resources PC-GP1-10TFE Polycarbonate, General Purpose, Wear Resistant, Low Flow
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow 5.0 - 12 g/10 min

@Load 1.20 kg,
Temperature 300 °C
5.0 - 12 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Polymer Resources PC-HM-FR1-[color]-3 Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilized
Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sampl..
Melt Flow 4.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 250 °C
4.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
Polymer Resources TP-FR-IM2-[color]-6 Polybutylene Terephthalate, Low Temperature Impact Modified, Flame Retardant
Polybutylene Terephthalate, Low Temperature Impact Modified, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, t..
Melt Flow 4.0 - 12 g/10 min
4.0 - 12 g/10 min
ASTM D1238
Polymer Resources TP-FV699 PBT, 10% Glass Reinforced Structural Foam Grade, Low Shrinkage
Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel..
Melt Flow 8.0 - 12 g/10 min
8.0 - 12 g/10 min
230/2.16; May be specified; ASTM D1238
Plastics Group Polifil® RMC-20 20% Calcium Carbonate-Reinforced Polypropylene, High Impact
Polifil® RMC series compounds are high impact polypropylenes reinforced with fine particle size calcium carbonate. In addition to the highest impact possible, they possess good stiffness, heat agin..
Melt Flow 8.0 - 12 g/10 min
8.0 - 12 g/10 min
230/2.16; May be specified; ASTM D1238
Plastics Group Polifil® RMT-40 40% Talc-Reinforced Polypropylene, High Impact
Polifil® RMT series compounds are high impact polypropylenes reinforced with asbestos-free talc. In addition to high impact strength, they possess a high flex modulus and high heat deflection resis..
Melt Flow 6.0 - 12 g/10 min

@Temperature 230 °C
6.0 - 12 g/10 min

@Temperature 446 °F
Condition L; ASTM D1238
A. Schulman PP 1349 Polypropylene Medium Impact Copolymer Polypropylene
DescriptionPolypropylene PP 1349 is a medium impact copolymer polypropylene.Information provided by A. Schulman.
Melt Flow 8.0 - 12 g/10 min
8.0 - 12 g/10 min
ISO 1133
Chengdu Polyster H3303 Thermoplastic Polyether-ester Elastomer (TPEE)
Low modulus molding and injection grade. Contains improved color- stable antioxidants. Excellent flex resistance at low temperatures. Moldable even in thin sections. Can be used in light-colored pro..
Melt Flow 8.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 190 °C
8.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
Cossa Polimeri ESTALENE EN 10 EC Modified Polyolefin Blend
Formulated for injection molding or extrusion of synthetic corksCertified according to FDA standardsInformation provided by Cossa Polimeri S.r.l.
Melt Flow 6.0 - 12 g/10 min
6.0 - 12 g/10 min
ASTM D1238
Buckeye Polymers BP FLEX D6020-08 BLK Thermoplastic Polyolefin
Product Information: TPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment.Product Features:High tear resist..
Melt Flow 8.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
AKG Polymers Vision PP PPH BL1004 Polypropylene Homopolymer Compound
Vision consists of a complete assortment of high-quality compounds based on industrial PP waste.Applications: Automotive, Non-food packaging, Storage/transport systems, Road and hydraulic Engineerin..
Melt Flow 8.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Aaron Industries AAROPRENE® CFIPP 2020 High Impact Calcium Carbonate Filled Polypropylene
AAROPRENE® CFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified.
Melt Flow 8.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Aaron Industries AAROPRENE® TFIPP 2020 High Impact Talc Filled Polypropylene
AAROPRENE® TFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified.
Melt Flow 8.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Aaron Industries AAROPRENE® TFIPP 2030 High Impact Talc Filled Polypropylene
AAROPRENE® TFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified.
Melt Flow 8.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Aaron Industries AAROPRENE® TFPP 2030 Talc Filled Polypropylene
AAROPRENE® TFPP 2000 Series Talc Reinforced CompoundsMelt flow index may be specified. Color may be specified.
Melt Flow 8.0 - 12 g/10 min
8.0 - 12 g/10 min
ASTM D1238
Buckeye Polymers BP RPP 1012 T BLK Polypropylene, Talc Filled
Product Information: Our Talc filled product lines exhibit excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and ..
Melt Flow 2.0 - 12 g/10 min
2.0 - 12 g/10 min
ASTM D1238
Buckeye Polymers BP RPP 2009 GK BLK Polypropylene, 20% Glass Filled
Product Information: Our glass reinforced product lines exhibit increased tensile strength, stiffness, and heat deflection. Highly optimized glass reinforced PP resins have successfully replaced en..
Melt Flow 8.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Aaron Industries AAROPRENE® CFIPP 2010 High Impact Calcium Carbonate Filled Polypropylene
AAROPRENE® CFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified.
Melt Flow 8.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Aaron Industries AAROPRENE® GFIPP 2020 High Impact Glass Filled Polypropylene
AAROPRENE® GFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified.
Melt Flow 6.0 - 12 g/10 min

@Load 1.00 kg,
Temperature 235 °C
6.0 - 12 g/10 min

@Load 2.20 lb,
Temperature 455 °F
3 min.; ASTM D1238
ALM D80-ST Nylon 11 SLS Prototyping Polymer
Unfilled, color stabilized nylon 11 material that is also stabilized to prevent premature thermal degradation. Parts produced from PA D80-ST exhibit superior mechanical properties. Relatively inexp..
Melt Flow 3.0 - 12 g/10 min

@Load 5.00 kg,
Temperature 200 °C
3.0 - 12 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
Aaron Industries AAROLENE® ARPS HI 100-3 Polystyrene Compounded Resin
AAROLENE® ARPS 100 Series Polystyrene Compounded ResinColor may be specified. Melt Flow Index may be specified.