Westlake EP413 Low Density Polyethylene

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Westlake Chemical Corporation
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Westlake EP413 Low Density Polyethylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

WESTLAKE polyethylene EP413 is a low-density polyethylene recommended for blown or cast film clarity applications. This material has very good optical properties, and is suggested for bakery films , produce bags, and general purpose clarity applications.Application/UsesGeneral purpose clarityMedium duty produce bagsBakery bagsBags for textile itemsFDA: This material complies with FDA regulations in 21 CFR, section 177.1520. Kosher Compliant.All information provided by Westlake Chemical

Physical Properties	Metric	English	Comments
Density	0.923 g/cc	0.0333 lb/in³	ASTM D1505
Thickness	31.8 microns	1.25 mil
Melt Flow	3.0 g/10 min @Load 2.16 kg, Temperature 190 °C	3.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	485 %	485 %	ASTM D882
Film Elongation at Break, TD	700 %	700 %	ASTM D882
Dart Drop	3.94 g/micron	100 g/mil	ASTM D1709
Film Tensile Strength at Break, MD	26.2 MPa	3800 psi	ASTM D882
Film Tensile Strength at Break, TD	17.2 MPa	2500 psi	ASTM D882
1% Secant Modulus, MD	186 MPa	27000 psi	ASTM D882
1% Secant Modulus, TD	207 MPa	30000 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	4.0 %	4.0 %	ASTM D1003
Gloss	80 %	80 %	at 45º; ASTM D2457

Processing Properties	Metric	English	Comments
Melt Temperature	182 - 199 °C	360 - 390 °F	with BUR of 1.5:1 or higher
Blow-up Ratio (BUR)	2.5	2.5

Descriptive Properties	Value	Comments
Process	Blown Film
	Film
Region	US & Canada	Bamberger Polymers Distribution