- Solvay Specialty Polymers Solef® 31508 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
Solvay Specialty Polymers Solef® 31508 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Solef® 31508 Polyvinylidene Fluoride (PVDF)
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solef® 31508 PVDF copolymer is a low viscosity and very flexible grade for Wire & Cable applications.Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.75 - 1.80 g/cc | 1.75 - 1.80 g/cc | ASTM D792 |
| Water Absorption | <= 0.040 % @Temperature 23.0 °C, Time 86400 sec |
<= 0.040 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.020 - 0.030 cm/cm | 0.020 - 0.030 in/in | |
| Melt Flow | 3.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 53 @Thickness 2.00 mm |
53 @Thickness 0.0787 in |
ASTM D2240 |
| Tensile Strength at Break | 14.0 - 30.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
2030 - 4350 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 14.0 - 35.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
2030 - 5080 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Elongation at Break | 350 - 600 % @Thickness 2.00 mm, Temperature 23.0 °C |
350 - 600 % @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Elongation at Yield | 10 - 12 % @Thickness 2.00 mm, Temperature 23.0 °C |
10 - 12 % @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Tensile Modulus | 0.400 - 0.600 GPa @Thickness 2.00 mm, Temperature 23.0 °C |
58.0 - 87.0 ksi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 1.0 mm/min; ASTM D638 |
| Izod Impact, Notched | 10.0 J/cm @Thickness 4.00 mm, Temperature 23.0 °C |
18.7 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F |
2 m/s, Partial Break; ASTM D6110 |
| Coefficient of Friction, Dynamic | 0.20 - 0.30 | 0.20 - 0.30 | vs. Itself; ASTM D1894 |
| Coefficient of Friction, Static | 0.20 - 0.40 | 0.20 - 0.40 | vs. Itself; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 5.0 - 10 @Load 1.00 kg |
5.0 - 10 @Load 2.20 lb |
CS-10 Wheel; ASTM D4060 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat of Fusion | 22.0 - 28.0 J/g | 9.46 - 12.0 BTU/lb | Crystallization Heat; ASTM D3417 |
| 23.0 - 29.0 J/g | 9.89 - 12.5 BTU/lb | ASTM D3417 | |
| CTE, linear, Parallel to Flow | 130 - 150 µm/m-°C @Temperature 0.000 - 40.0 °C |
72.2 - 83.3 µin/in-°F @Temperature 32.0 - 104 °F |
ASTM D696 |
| Specific Heat Capacity | 1.20 J/g-°C @Temperature 23.0 °C |
0.287 BTU/lb-°F @Temperature 73.4 °F |
ASTM E968 |
| 1.60 J/g-°C @Temperature 100 °C |
0.382 BTU/lb-°F @Temperature 212 °F |
ASTM E968 | |
| Thermal Conductivity | 0.200 W/m-K @Temperature 23.0 °C |
1.39 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
ASTM C177 |
| Melting Point | 167 - 171 °C | 333 - 340 °F | ASTM D3418 |
| Crystallization Temperature | 125 - 131 °C | 257 - 268 °F | Peak, DSC; ASTM D3418 |
| Vicat Softening Point | 110 °C | 230 °F | Rate A (50°C/h), Loading 2 (50 N); ASTM D1525 |
| Glass Transition Temp, Tg | -28.0 °C | -18.4 °F | ASTM D4065 |
| Flammability, UL94 | V-0 @Thickness 0.100 mm |
V-0 @Thickness 0.00394 in |
UL 94 |
| Oxygen Index | 48 % @Thickness 3.00 mm |
48 % @Thickness 0.118 in |
ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 7.0 @Frequency 1000 Hz, Temperature 23.0 °C |
7.0 @Frequency 1000 Hz, Temperature 73.4 °F |
ASTM D150 |
| Dielectric Strength | 20.0 - 25.0 kV/mm @Thickness 1.00 mm, Temperature 23.0 °C |
508 - 635 kV/in @Thickness 0.0394 in, Temperature 73.4 °F |
ASTM D149 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Features | Copolymer | |
| Good Flexibility | ||
| Low Viscosity | ||
| Forms | Granules | |
| Generic | PVDF | |
| Uses | Wire & Cable Applications |
Users viewing this material also viewed the following:
- Greene Tweed FLUORAZ® 890 Fluoroelastomer, FEPM
- Special Metals UDIMET® alloy D-979 Fe-Ni Alloy
- Teknor Apex Fireguard® 910-LBF Polyvinyl Chloride, Flexible
- Solvay BRICORR® 75 TETRAKIS(HYDROXYMETHYL)PHOSPHONIUM SULPHATE (THPS)
- ThyssenKrupp N-A-XTRA® 620 Structural Steel
- A. Schulman POLYFORT™ FPP 4529 Mineral Filled Copolymer Polypropylene
- Master Bond EP41SMed Two Component, Low Viscosity, USP Class VI Epoxy System
- Clariant Renol 66G15BL-195 Blue Nylon 66, 15% Glass Fiber Reinforced
- Eurotec® Tecopet® PT74 GR45 BK002 PR PET, 45% glass fiber reinforced, high heat stabilized, black
- 3M 414DL Flexomount™ Solid Printing Tapes
Copyright © lookpolymers.com All Rights Reserved