- Polyram PlusTek PA340S05 Nylon 6.6 for Injection Molding, 5% Glass-beads Reinforced, Heat Stabilized
Polyram PlusTek PA340S05 Nylon 6.6 for Injection Molding, 5% Glass-beads Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA340S05 Nylon 6.6 for Injection Molding, 5% Glass-beads Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
5% Glass-beads reinforced Nylon 6.6, heat stabilized for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 4.4 % | 4.4 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 9.45 % | 9.45 % | ISO 62 |
| Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 2.85 GPa | 413 ksi | ISO 527 |
| Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 258 °C | 496 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- Pyrotek Vacuum Formed Shapes for Continuous Sheet Casting
- Michelman® Topaz Indicator 17 Solution
- Teknor Apex APEX® 97-G0029C-82 Polyvinyl Chloride, Flexible
- Solvay GEROPON® SBL-203 Surfactant
- CeramTec V 679 Alumina, 99.7%
- Washington Penn PPH2UFO Polypropylene, Unfilled
- Wellman Wellamid® WE1408 13% Glass Fiber Reinforced Engineering Grade Nylon 66
- Dow DOWLEX™ 2553 Linear Low Density Polyethylene, Narrow MW Distribution
- BASF Ultramid® NFX-0102 NF2004 30% Glass Filled PA66 (Dry)
Copyright © lookpolymers.com All Rights Reserved