Polyram PlusTek PA801 Nylon 6.6 Copolymer for Injection Molding, Impact Modified

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer Polyram
Trade Name PlusTek
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polyram PlusTek PA801 Nylon 6.6 Copolymer for Injection Molding, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Impact modified Nylon 6.6 copolymer for injection molding application.Information provided by Polyram.
Physical Properties Metric English Comments
Density 1.09 g/cc
0.0394 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 2.1 %
2.1 %
50% RH; ISO 62
Linear Mold Shrinkage 0.014 - 0.018 cm/cm
0.014 - 0.018 in/in
ISO 2577
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
Tensile Strength, Yield 70.0 MPa
10200 psi
ISO 527
Elongation at Break 30 %
30 %
ISO 527
Tensile Modulus 2.50 GPa
363 ksi
ISO 527
Flexural Strength 110 MPa
16000 psi
ISO 178
Flexural Modulus 2.40 GPa
348 ksi
ISO 178
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 256 °C
493 °F
ISO 11357
Maximum Service Temperature, Air 70.0 °C
158 °F
Continuous use
180 °C
356 °F
Short peaks operation
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ISO 75
Flammability, UL94 HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
 3.2

@Frequency 1.00e+6 Hz
 IEC 60250
Dielectric Strength 32.0 kV/mm
813 kV/in
IEC 60250