A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer

Category	Polymer , Thermoplastic , Ionomer , Ionomer, Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

DescriptionFormion® FI 120 is a non-reinforced, transparent, injection molding grade Zinc Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and low stiffness. ApplicationFormion® FI 120 is targeted for non painted, mold-in-color, exterior or interior appearance application requiring high or low gloss, and excellent colorability or transparency. It can also be used in applications requiring adhesion to metal. Information provided by A. Schulman.

Physical Properties	Metric	English	Comments
Specific Gravity	0.960 g/cc	0.960 g/cc	ISO 1183/1
Linear Mold Shrinkage	0.0060 - 0.018 cm/cm @Thickness 3.20 mm, Time 259000 sec	0.0060 - 0.018 in/in @Thickness 0.126 in, Time 72.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	57	57	15 sec delay; ISO 868
	63	63	Instantaneous; ISO 868
Tensile Strength, Ultimate	21.0 MPa	3050 psi	at max load; ISO 527
Elongation at Break	225 %	225 %	ISO 527
Flexural Modulus	0.227 GPa	32.9 ksi	Tangent; ISO 178
Izod Impact, Notched (ISO)	NB	NB	ISO 180

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	38.0 °C @Thickness 3.17 mm	100 °F @Thickness 0.125 in	ISO 75

Optical Properties	Metric	English	Comments
Transmission, Visible	90 %	90 %	transparent; thickness not quantified