Polykemi AB POLYfill PPC 12000 Polypropylene Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer Polykemi AB
Trade Name POLYfill
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYfill PPC 12000 Polypropylene Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 0.900 g/cc
0.0325 lb/in³
ISO 1183
Linear Mold Shrinkage 0.015 - 0.018 cm/cm
0.015 - 0.018 in/in
With Flow; ISO 2577
0.015 - 0.018 cm/cm
0.015 - 0.018 in/in
Across Flow; ISO 2577
Melt Index of Compound 12 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 12 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 25.0 MPa
<= 3630 psi
ISO/R527
Elongation at Yield 8.0 %
8.0 %
ISO/R527
Flexural Modulus 1.30 GPa

@Temperature 23.0 °C
 189 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.600 J/cm²

@Temperature -20.0 °C
 2.86 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
1.00 J/cm²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 56.0 °C
133 °F
120°C/h; ISO 75/1
Vicat Softening Point 146 °C

@Load 1.00 kg
 295 °F

@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 2.00 mm
 HB

@Thickness 0.0787 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
 1200 °F

@Thickness 0.0787 in
 IEC 695-2-1