Polyram PlusTek PA804 Nylon 6.6 for Injection Molding, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA804 Nylon 6.6 for Injection Molding, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact modified Nylon 6.6 for injection molding application.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 5.5 % | 5.5 % | ISO 62 |
| Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527 |
| Elongation at Break | 50 % | 50 % | ISO 527 |
| Tensile Modulus | 2.07 GPa | 300 ksi | ISO 527 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 11357 |
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | Continuous use |
| 180 °C | 356 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 100 kV/mm | 2540 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- MV Labs NA870 Na2CO4 Sodium oxalate
- Polimeri Europa Europrene® SOL T 9133 Styrene - Isoprene Block Copolymer
- Advanced Elastomer Systems Trefsin® 3101-85 W305 Thermoplastic Rubber (discontinued **)
- Overview of materials for Polyetherimide (PEI), Carbon Fiber Filled
- Shin-Etsu Silicones X-821-1276 Fluid
- Covestro Apec® HT KU 1-9333 High-Heat Polycarbonate
- Elektro-Isola Etronax MF Phenolic, Cotton Fabric Reinforcement, Brown, Sheets
- Arkema Group Rilsan® MA 4420 Nylon 12, Flexible Tubing Grade (Conditioned)
- Arlon 51106RB015D Silicone Rubber/Fiberglass Laminate
- Barlog Plastics KEBAFORM C 90 M POM Copolymer unreinforced, optimized crystallization
Copyright © lookpolymers.com All Rights Reserved