Total PPC 7810 Polypropylene, Heterophasic Copolymer, High Impact
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | Total Atofina |
| Trade Name | PPC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Total PPC 7810 Polypropylene, Heterophasic Copolymer, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polypropylene PPC 7810 is a very high impact heterophasic copolymer with a Melt Flow index of 15 g/10 min.Polypropylene PPC 7810 has been specially developed for high impact and heavy duty applications like automotive bumpers, crates and pails.Information provided by Total Petrochemicals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.905 g/cc | 0.905 g/cc | ISO 1183 |
| Bulk Density | 0.525 g/cc | 0.0190 lb/in³ | ISO 1183 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 78 | 78 | ISO 2039-2 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO 527-2 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527-2 |
| Tensile Modulus | 1.05 GPa | 152 ksi | ISO 527-2 |
| Flexural Modulus | 0.950 GPa | 138 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -20.0 °C |
3.81 ft-lb/in² @Temperature -4.00 °F |
ISO 180 |
| >= 50.0 kJ/m² @Temperature 23.0 °C |
>= 23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact, Notched | 0.850 J/cm² @Temperature -20.0 °C |
4.04 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| >= 5.00 J/cm² @Temperature 23.0 °C |
>= 23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | 120°C per hour; ISO 752 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | 120°C per hour; ISO 752 |
| Vicat Softening Point | 65.0 °C @Load 5.10 kg |
149 °F @Load 11.2 lb |
50°C per hour; ISO 306 |
| 135 °C @Load 1.02 kg |
275 °F @Load 2.25 lb |
50°C per hour; ISO 306 |