Sharadaa Ceramics REFPLAST 60 60% Alumina Plastic

Category Ceramic , Oxide , Aluminum Oxide
Manufacturer Sharadaa Ceramics
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Sharadaa Ceramics REFPLAST 60 60% Alumina Plastic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nature of bond: Chemical-CeramicInstallation: Pneumatic rammingInformation provided by Sharadaa Ceramics Pvt. Ltd.
Physical Properties Metric English Comments
Density 2.50 g/cc
0.0903 lb/in³
Specification, After dried @ 110°C/24 hrs
2.52 g/cc
0.0910 lb/in³
Typical value, After dried @ 110°C/24 hrs
Grain Size <= 4000 µm
<= 4000 µm
Mechanical Properties Metric English Comments
Compressive Strength >= 9.81 MPa

@Temperature 110 °C,
Time 86400 sec
 >= 1420 psi

@Temperature 230 °F,
Time 24.0 hour
 Cold Crushing, Specification, After drying @ 110°C
10.8 MPa

@Temperature 110 °C,
Time 86400 sec
 1560 psi

@Temperature 230 °F,
Time 24.0 hour
 Cold Crushing, Typical Value, After drying @ 110°C
>= 24.5 MPa

@Temperature 800 °C,
Time 10800 sec
 >= 3560 psi

@Temperature 1470 °F,
Time 3.00 hour
 Cold Crushing, Specification, After firing @ 800°C
26.0 MPa

@Temperature 800 °C,
Time 10800 sec
 3770 psi

@Temperature 1470 °F,
Time 3.00 hour
 Cold Crushing, Typical Value, After firing @ 800°C
>= 34.3 MPa

@Temperature 1100 °C,
Time 10800 sec
 >= 4980 psi

@Temperature 2010 °F,
Time 3.00 hour
 Cold Crushing, Specification, After firing @ 1100°C
37.7 MPa

@Temperature 1100 °C,
Time 10800 sec
 5460 psi

@Temperature 2010 °F,
Time 3.00 hour
 Cold Crushing, Typical Value, After firing @ 1100°C
>= 44.1 MPa

@Temperature 1400 °C,
Time 10800 sec
 >= 6400 psi

@Temperature 2550 °F,
Time 3.00 hour
 Cold Crushing, Specification, After firing @ 1400°C
47.6 MPa

@Temperature 1400 °C,
Time 10800 sec
 6900 psi

@Temperature 2550 °F,
Time 3.00 hour
 Cold Crushing, Typical Value, After firing @ 1400°C
Thermal Properties Metric English Comments
Thermal Conductivity 1.53 W/m-K

@Temperature 600 °C
 10.6 BTU-in/hr-ft²-°F

@Temperature 1110 °F
1.55 W/m-K

@Temperature 400 °C
 10.8 BTU-in/hr-ft²-°F

@Temperature 752 °F
1.57 W/m-K

@Temperature 200 °C
 10.9 BTU-in/hr-ft²-°F

@Temperature 392 °F
Maximum Service Temperature, Air 1600 °C
2910 °F
Component Elements Properties Metric English Comments
Al2O3 60 %
60 %
Fe2O3 2.0 %
2.0 %
Descriptive Properties Value Comments
Base Material Synthetic Alumina Base
PCE Orton 33
Permanent Linear Change -0.17
Typical Value, After drying @ 1100°C/3hrs
-0.25
Typical Value, After drying @ 1400°C/3hrs
-1.5 - 1.5%
Specification, After drying @ 1100°C/3hrs
-1.5 - 1.5%
Specification, After drying @ 1400°C/3hrs
Refractoriness 1763°C