SABIC Innovative Plastics Ultem LTX921A PEI Blend
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem LTX921A PEI Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Post-industrial recycle based, 20% glass fiber filled, high flow Polyetherimide blend. ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D 792 |
| Melt Flow | 10 g/10 min @Load 6.60 kg, Temperature 337 °C |
10 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 6.96 GPa | 1010 ksi | 5 mm/min; ASTM D 638 |
| Flexural Strength | 193 MPa | 28000 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Flexural Modulus | 7.23 GPa | 1050 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 4.27 J/cm @Thickness 3.20 mm |
8.00 ft-lb/in @Thickness 0.126 in |
reverse notched; ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 198 °C @Thickness 6.40 mm |
388 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |