Polymer Property : Tensile Modulus = 1010 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Modulus 6.95 GPa
1010 ksi
Radici Radilon® S RCV3015 (dry) Nylon 6
Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group.
Tensile Modulus 6.94 GPa
1010 ksi
same value from ASTM and ISO test.
BASF Capron® HPN 9233G 33% Glass-Filled Nylon 6 (Conditioned)  (discontinued **)
Capron HPN 9233G is a 33% glass reinforced polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface aesthetics. It is..
Tensile Modulus 6.96 GPa
1010 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM AR9200 PEI
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
Tensile Modulus 6.96 GPa
1010 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM AR9200 PEI (Asia Pacific)
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
Tensile Modulus 6.96 GPa
1010 ksi
5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem LTX921A PEI Blend
Post-industrial recycle based, 20% glass fiber filled, high flow Polyetherimide blend. ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
Tensile Modulus 6.96 GPa
1010 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON DE002ER PC
LNP STAT-KON* DE002ER is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Easy Molding. Mold Release, Electrically Conductive.
Tensile Modulus 6.96 GPa
1010 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON DE002ER PC (Asia Pacific)
LNP STAT-KON* DE002ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding.
Tensile Modulus 6.95 GPa
1010 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON DX11411 PC
LNP* STAT-KON* DX11411 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive.
Tensile Modulus 6.93 GPa
1010 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON MX01739C PP
LNP* SAT-KON* MX01739C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System.
Tensile Modulus 6.95 GPa
1010 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF0049P PC
LNP* Thermocomp* DF0049P is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Exceptional Processing, Flame Retardant.
Tensile Modulus 6.96 GPa
1010 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DX06411H PC
LNP* THERMOCOMP* DX06411H is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare.
Tensile Modulus 6.99 GPa
1010 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DX06411H PC
LNP* THERMOCOMP* DX06411H is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare.
Tensile Modulus 6.93 GPa
1010 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP LF003 PEEK
LNP* THERMOCOMP* LF003 is a compound based on Polyetheretherketone resin containing 15% Glass Fiber.
Tensile Modulus 6.93 GPa
1010 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP LF003 PEEK (Asia Pacific)
LNP* Thermocomp* LF003 is a compound based on Polyetheretherketone resin containing Glass Fiber.
Tensile Modulus 6.93 GPa
1010 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp LF003E PEEK
LNP* Thermocomp* LF003E is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Tensile Modulus 6.93 GPa
1010 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp LF003E PEEK (Asia Pacific)
LNP* Thermocomp* LF003E is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Modulus 6.95 GPa
1010 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF0049P PC (Asia Pacific)
LNP* Thermocomp* DF0049P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing, Flame Retardant.
Tensile Modulus 6.93 GPa
1010 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP VERTON MV006BS PP
LNP* VERTON* MV006BS is a compound based on Polypropylene resin containing 30% Long Glass Fiber. Added features of this grade include: Heat Stabilized, Burst Pressure, Structural, Chemically Coupl..