SABIC Innovative Plastics Lexan® SLX1482T PC Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® SLX1482T PC Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium viscosity PC Copolymer, enhanced UV stabilization. Transprarent and tinted colors. Higher mold release content than SLX1432T.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Water Absorption 0.12 %

@Time 86400 sec
0.12 %

@Time 24.0 hour
ASTM D 570
Moisture Absorption at Equilibrium 0.17 %
0.17 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.25 %

@Temperature 23.0 °C
0.25 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 9.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
9.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 69.0 MPa
10000 psi
50 mm/min; ISO 527
72.0 MPa
10400 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 65.0 MPa
9430 psi
50 mm/min; ISO 527
67.0 MPa
9720 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 110 %
110 %
Type I, 50 mm/min; ASTM D 638
110 %
110 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
Type I, 50 mm/min; ASTM D 638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.55 GPa
370 ksi
50 mm/min; ASTM D 638
2.55 GPa
370 ksi
1 mm/min; ISO 527
Flexural Yield Strength 105 MPa
15200 psi
2 mm/min; ISO 178
105 MPa
15200 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.50 GPa
363 ksi
2 mm/min; ISO 178
2.50 GPa
363 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.980 J/cm

@Temperature -30.0 °C
1.84 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
7.00 J/cm

@Temperature 23.0 °C
13.1 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 26.0 J/cm

@Temperature 23.0 °C
48.7 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
25.0 kJ/m²

@Temperature 23.0 °C
11.9 ft-lb/in²

@Temperature 73.4 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
3.00 J/cm²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Impact Test 77.0 J

@Temperature 23.0 °C
56.8 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
85.0 J

@Temperature -40.0 °C
62.7 ft-lb

@Temperature -40.0 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 66.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
37.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
66.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
37.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 64.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
64.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 130 °C

@Thickness 3.20 mm
266 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 116 °C
241 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
118 °C

@Thickness 3.20 mm
244 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 135 °C
275 °F
Rate B/50; ASTM D 1525
135 °C
275 °F
Rate B/50; ISO 306
137 °C
279 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
UL 94
Optical Properties Metric English Comments
Refractive Index 1.59
1.59
ASTM D 542
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2